采用种子乳液聚合的方法合成核壳型丙烯酸酯微球,将4种增塑剂邻苯二甲酸二异壬酯(DINP)、乙酰柠檬酸三丁酯(ATBC)、二乙酸甘油酯(GD)、磷酸三丁酯(TBP)分别与丙烯酸酯聚合物粉末混合制备环保型丙烯酸酯类聚合物溶胶.采用TG,SEM、万能力学测试仪、DMA等分析仪器表征了溶胶的耐热性、表面形貌、拉伸性能及动态力学性能;结果表明:以DINP为增塑剂制备的丙烯酸酯溶胶,与碳酸钙的相容性较好,拉伸强度达到1.01 MPa,耐热性好,是比较理想的增塑剂.
参考文献
| [1] | A.Jimenez;J.Lopez;A.Iannoni;J.M.Kenny .Formulation and Mechanical Characterization of PVC Plastisols Based on Low-Toxicity Additives[J].Journal of Applied Polymer Science,2001(8):1881-1890. |
| [2] | ETO H;SAKAI O;HIGUCHI A et al.Acrylic resin plastisol coating compound[P].US,6916869,2005-07-12. |
| [3] | Wang GJ;Wang XD;Jin RG .Preparation and properties of novel plastisols based on acrylic core-shell lattices[J].Colloid and polymer science,2004(1):98-106. |
| [4] | KASAI T;TSUCHIHASHI T .Fine polymer particles for plastisol,process for producing the same,and halogen-free plastisol composition and article made with the same[P].US,6894108,2005-05-17. |
| [5] | MAE S .(Meth)acrylic polymer particle,method for producing the same,plastisol composition made from the polymer particle,and article made from the plastisol composition[P].US,20100069566A1,2010-05-18. |
| [6] | TOSHIHIRO KASAI N .Acrylic polymer fine particles and plastisol using the same[P].US,6433048,2002-08-13. |
| [7] | 黄宁.常用分析仪器在涂料用树脂研发中的应用（二）[J].涂料工业,2007(12):51-55. |
| [8] | 过梅丽;陈金风.美国热分析仪器公司(TA Instruments)动态力学分析仪(DMA2980)[J].现代科学仪器,1996(03):55-58. |
| [9] | 邓友娥,章文贡.动态机械热分析技术在高聚物性能研究中的应用[J].实验室研究与探索,2002(01):38-39,62. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%