采用自由基溶液聚合法,以甲基丙烯酸四氢糠基酯(THFMA)、甲基丙烯酸羟乙酯(HEMA)、甲基丙烯酸二甲胺基乙酯(DMAEMA)、甲基丙烯酸异冰片酯(IBOMA)、N-羟甲基丙烯酰胺(NMA)等单体合成了高附着力丙烯酸阴极电泳涂料用树脂.研究树脂漆膜外观及性能的几种影响因素.实验结果表明:THFMA用量为15％,以偶氮二异丁腈为引发剂,槽液pH控制在5.8左右,可得到平整丰满漆膜,其附着力为0级,光泽可达130.4,膜厚为21.4μm.可广泛应用与五金、汽车等行业.
参考文献
| [1] | 张鹏;王兆华.丙烯酸树脂防腐蚀涂料及应用[M].北京:化学工业出版社,2003:2-3. |
| [2] | 谢志刚,江燕红,周乐奋,廖瑞莹,邱星林.高附着力丙烯酸树脂的研制[J].涂料工业,2005(07):30-33. |
| [3] | 周铭.涂膜附着机理与附着力促进剂的选择[J].现代涂料与涂装,2007(08):1-3. |
| [4] | JOHN J A;MARTA M C;SARAH H et al.Porous methacrylate tissue engieering scaffolds:using carbon dioxide to control porosity and interconnectivity[J].Journal of Materials Science: Materials in Medicine,2006,41:4197-4204. |
| [5] | Hutcheon GA.;Davies MC.;Downes S. .Interactions of chondrocytes with methacrylate copolymers[J].Journal of Materials Science. Materials in Medicine,1998(12):815-818. |
| [6] | Sawtell RM;Downes S;Patel MP;Clarke RL;Braden M .Heterocyclic methacrylates for clinical applications further studies of water sorption[J].Journal of Materials Science. Materials in Medicine,1997(11):667-674. |
| [7] | Labella R.;Clarke RL.;Davy KWM.;Braden M. .THFMA IN DENTAL MONOMER SYSTEMS[J].Biomaterials,1996(4):431-436. |
| [8] | 王文浩;刘慧 .耐油羟基丙烯酸树脂及其制备方法和用途[P].CN,101928364A,2010-12-19. |
| [9] | 陈炳耀;张意田;陈亮 等.一种低味双组分丙烯酸酯胶黏剂[P].CN,101705057A,2010-05-12. |
| [10] | 蒋建平,李小玉.阴极电泳涂料用丙烯酸改性环氧树脂的制备[J].涂料工业,2010(06):44-46,51. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%