选择环氧官能度适中的酚醛环氧树脂作为基料,以脂环胺作为固化剂,制备了常温固化酚醛环氧涂料.考察了脂环胺的加成改性对其抗发白性和黏度的影响；探讨了3种脂环胺的耐化学品性差异；研究了苯甲醇对酚醛环氧漆膜的固化程度和耐化学品性的影响；分析了偶联剂对涂膜的抗阴极剥离作用.结果表明:选用官能度适中的DEN431作为酚醛环氧树脂；活泼氢当量为65的改性4,4’-二氨基二环己基甲烷作为固化剂；以苯甲醇作为增塑剂,其用量为酚醛环氧树脂的7.5％；以KH-550作为偶联剂,其用量为酚醛环氧树脂的0.5％(质量分数,下同)；以DMP-30作为促进剂,其用量为酚醛环氧树脂的0.8％,得到耐化学品性与耐温性优异的常温固化酚醛环氧涂料.
参考文献
| [1] | 《涂料工业》编委会.涂料工业上册[M].北京:化学工业出版社,1997:646-653. |
| [2] | 李国荣;张慰盛;管从胜.重防腐涂料[M].北京:化学工业出版社,1999:28-29. |
| [3] | WISANRAKKIT G;GILLHAM J K .The glass transition temperature (Ts) as an index of chemical conversion for a high-Ts anine/epoxy system:chemical and diffusion-contnlled reaction kinetics[J].Journal of Applied Polymer Science,1990,41(11/12):2885. |
| [4] | 胡玉明;吴良义.固化剂[M].北京:化学工业出版社,2004:141-149. |
| [5] | JAMES A;HERBERT A NEWEY .Use of 2,5-dimethy1-2,5-hexane diamine as a curing agent for epoxy resins[P].US,4252936,1981-02-24. |
| [6] | Frederick H. Walker;Michael Cook;Gamini Vedage .Dimethyl secondary amine chain extenders: a conceptual approach to in situ generation of advanced epoxy resins for rapid cure, low VOC coatings[J].JCT research,2009(3):283-313. |
| [7] | Frederick A. Pfaff .Growing more ductile epoxies: an essential work of fracture study[J].JCT research,2007(2):151-159. |
| [8] | CALBO L J.涂料助剂大全[M].上海:上海科学技术文献出版社,2000:556-557. |
| [9] | JOHN SHOMER .Hardener for epoxy resins[P].US,5958593,1999-09-28. |
| [10] | MAURICE J;MARKS R;VERNON SNELGROVE .Effect of conversion on the structure-property relationships of amine-curd epoxy thermosets[J].Applied Materials and Interfaces,2009,1(04):921-926. |
| [11] | VERCHHRE D;SAUTEREAU H;PASCAULT J P .Buildup of epoxyeycloaliphatic amine networks,kinetics,vitrification,and gelation[J].Macromolecules,1990,23(03):725-731. |
| [12] | Kroutilova I;Matejka L;Sikora A;Soucek K;Stas L .Curing of epoxy systems at sub-glass transition temperature[J].Journal of Applied Polymer Science,2006(6):3669-3676. |
| [13] | 周钟瑔.阴极保护条件下环氧基界面粘附性研究[J].腐蚀科学与防护技术,1998(03):146. |
| [14] | Harun MK;Marsh J;Lyon SB .The effect of surface modification on the cathodic disbondment rate of epoxy and alkyd coatings[J].Progress in Organic Coatings: An International Review Journal,2005(4):317-321. |
| [15] | SATHYANARAYANA M N;YASEEN M .Role of promoters in improving adhesion of organic coatings to a substrate[J].Progsess in Organic Coatings,1995,26(02):275-313. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%