采用聚丁二醇(PBG)、2,4 -甲苯二异氰酸酯、二羟甲基丙酸(DMPA)和丙烯酸羟乙酯合成了紫外光固化水性聚氨酯丙烯酸酯树脂,利用FT-IR对树脂进行了表征,探讨了树脂亲水基团含量和中和度对乳液性能的影响,分析表征了固化膜的基本性能.结果表明:乳液的粒径随着-COOH含量的提高而下降,乳液的分散性、稳定性及黏度随-COOH含量增加而增大;乳液黏度在中和度为90%时达到最高6.222 mPa·s,粒径达到最小59.8 nm.固化膜的吸水率随-COOH含量的增加而上升,固化膜对PVC板具有很好的附着力,其铅笔硬度随着DMPA/PBG比例的增加而上升.
参考文献
[1] | 何勇,聂俊.水性光固化材料[J].涂料技术与文摘,2007(06):1-5,62. |
[2] | Kim BK.;Seo JW.;Jeong HM. .Morphology and properties of waterborne polyurethane/clay nanocomposites[J].European Polymer Journal,2003(1):85-91. |
[3] | Wicks ZW.;Wicks DA.;Rosthauser JW. .Two package waterborne urethane systems [Review][J].Progress in Organic Coatings: An International Review Journal,2002(2):161-183. |
[4] | D.K.Chattopadhyay;K.V.S.N.Raju .Structural engineering of polyurethane coatings for high performance applications[J].Progress in Polymer Science,2007(3):352-418. |
[5] | Elena Orgiles-Calpena;Francisca Aran-Ais;Ana M. Torro-Palau .Addition of different amounts of a urethane-based thickener to waterborne polyurethane adhesive[J].International Journal of Adhesion & Adhesives,2009(3):309-318. |
[6] | 万成龙,贺建芸.水性紫外光固化聚氨酯丙烯酸酯树脂的合成[J].北京化工大学学报(自然科学版),2010(05):93-97. |
[7] | 魏丹,叶代勇,黄洪,陈焕钦.多重交联紫外光固化水性聚氨酯涂料[J].涂料工业,2008(05):4-7. |
[8] | 王震,季永新,胡格非.合成革用水性聚氨酯的制备[J].聚氨酯工业,2011(02):40-43. |
[9] | 陈梁,吕满庚.丙烯酸改性水性聚氨酯研究进展[J].涂料工业,2005(03):39-44. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%