通过超声法制备了超细涂料色浆,并将其应用到阴极电泳漆中.考察了超细化前后涂料色浆的平均粒径、Zeta电位的变化,比较分析了超细涂料色浆与普通涂料色浆用于阴极电泳漆时漆液稳定性、漆膜沉积量、颜色深度、外观的区别.实验结果表明:超细涂料色浆的平均粒径仅为196 nm,Zeta电位为30 mV且分布均匀.用超细涂料色浆配制的电泳漆液具有较高的离心稳定性.相比于含普通涂料色浆的阴极电泳漆,含有超细涂料色浆的阴极电泳漆的漆膜的电沉积量稍高,而且更加均匀、平整、细腻.
参考文献
| [1] | PADGET J C .Polymers for water-based coatings system overview[J].Journal of Coatings Technology,1981,66(839):89-105. |
| [2] | Kim YB;Kim HK;Hong JW .UV-curable methacrylic epoxy dispersions for cationic electrodeposition coating[J].Journal of Applied Polymer Science,2006(6):5566-5570. |
| [3] | 李田霞,陈存华.阴极电泳涂料的发展趋势[J].电镀与精饰,2007(01):22-26. |
| [4] | GUOBEI C;FRANK N J .Low-temperature curing higher-solids polyester coatings with melamine-formaldehyde resin crosslinkers[J].Journal of Coatings Technology,1993,65(819):43-48. |
| [5] | Zhang, J;Wu, CY .Corrosion protection behavior of AZ31 magnesium alloy with cathodic electrophoretic coating pretreated by silane[J].Progress in Organic Coatings: An International Review Journal,2009(4):387-392. |
| [6] | Gao Yong;Mulenda Tshomba Kays;Shi Yi-Feng;Yuan Wei-Kang .Fine particles preparation of Red Lake C Pigment by supercritical fluid[J].The Journal of Supercritical Fluids,1998(1/3):369-374. |
| [7] | 伍金平,杜长森,周华,吕仕铭.通用型阴极电泳色浆的制备分析[J].表面技术,2007(02):65-66,83. |
| [8] | 伍金平,杜长森,吕仕铭.水性色浆的性能分析[J].化学建材,2007(04):16-18. |
| [9] | 周春隆.有机颜料粒子表面极性调整技术进展[J].精细与专用化学品,2007(17):5-8. |
| [10] | P.M.T.Cavalcante;M.Dondi;G.Guarini .Colour performance of ceramic nano-pigments[J].Dyes and Pigments,2009(2):226-232. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%