涂料应用中往往会出现一些人们肉眼难以察觉的损伤.若存在一种自修复材料,能够在涂层破损时发挥自愈作用,则可以大大延长涂料的寿命.本研究制备了一种微胶囊,以填料的方式加入到涂料中,可对受损涂层起到自修复的作用.采用原位聚合法,以KH-550改性的双酚F环氧树脂为囊芯原料,合成脲醛树脂包裹环氧树脂的微胶囊.探讨了原料比、乳化剂用量、搅拌速率等因素对微胶囊性能的影响.结果表明:当囊壁与囊芯的质量比为1∶0.8,乳化剂SDBS用量为0.8％,搅拌速率为300 r/min,酸化时间为2～3h,控温60℃时微胶囊的各项性能较好.
参考文献
| [1] | M.R. Kess1er;S.R. White .Self-activated healing of delamination damage in woven composites[J].Composites, Part A. Applied science and manufacturing,2001(5):683-699. |
| [2] | Suryanarayana C;Rao KC;Kumar D .Preparation and characterization of microcapsules containing linseed oil and its use in self-healing coatings[J].Progress in Organic Coatings: An International Review Journal,2008(1):72-78. |
| [3] | 李岚 .用于复合材料自修复的微胶囊的合成[D].西北工业大学,2006. |
| [4] | 赫焕英 .复合材料自修复用微胶囊的制备[D].哈尔滨:哈尔滨工业大学,2007. |
| [5] | 范传杰 .脲醛树脂壁材微胶囊的制备及其性能研究[D].华东理工大学,2010. |
| [6] | B.J. Blaiszik;N.R. Sottos;S.R. White .Nanocapsules for self-healing materials[J].Composites science and technology,2008(3/4):978-986. |
| [7] | 叶都长,张力,孟春玲.微胶囊自修复技术及其在聚合物基复合材料中的应用[J].北京工商大学学报(自然科学版),2008(02):27-30. |
| [8] | E.N.Brown;M.R.Kessler;N.R.Sottos;S.R.White .In situ poly(urea-formaldehyde)microencapsulation of dicyclopentadiene[J].Journal of Microencapsulation: Microcapsules Liposomes Nanoparticles Microcells Microspheres,2003(6):719-730. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%