用异氰酸酯三聚体与二羟甲基丙酸(DMPA)先进行扩链反应,蒋用3,5-二甲基吡唑(DMP)将剩余的异氰酸酯基封闭,然后用二甲基乙醇胺(DMEA)中和成盐,制得可水分散型封闭异氰酸酯固化剂(WBI),并讨论了封闭比例[n(-H)∶n(-NCO)]、DMPA用量、反应温度、反应时间对制备水分散型封闭异氰酸酯固化剂的影响.采用傅里叶变换红外光谱(FT -IR)和差示扫描量热法(DSC)对封闭固化剂的结构进行了表征及分析,结果表明得到了预定结构产物,并且制备的封闭型多异氰酸酯固化剂可在较低温度( 130～ 150℃)实现解封.用合成的封闭异氰酸酯与环氧改性丙烯酸树脂制备了水性玻璃烘烤涂料,并对涂膜性能作了初步探讨.
参考文献
| [1] | AMOLD R G;NELSON J A;VERBANC J .Recent advances in isocyanate chemistry[J].Chemical Reviews,1957,57(01):47-76. |
| [2] | 张春华;亢茂青;王心葵.封端异氰酸酯研究进展Ⅰ[J].化工新型材料,1996(12):21-24. |
| [3] | 张春华;亢茂青;王心葵.封端异氰酸酯研究进展Ⅱ[J].化工新型材料,1997(01):24-27. |
| [4] | 王靖 .水基型聚氨酯的聚异氰酸酯交联剂[J].世界橡胶工业,1998,25(01):25-32. |
| [5] | SHARMA B;UBAGHS L;KEUL H et al.Synthesis and characterization of alternating poly(amide urethanes) from caprolactam,amino alcohols,and diphenyl carbonate[J].Polymer,2004,45:5427-5440. |
| [6] | Yeh JM;Yao CT;Hsieh CF;Yang HC;Wu CP .Preparation and properties of amino-terminated anionic waterborne-polyurethane-silica hybrid materials through a sol-gel process in the absence of an external catalyst[J].European Polymer Journal,2008(9):2777-2783. |
| [7] | ZENO W W;DOUGLAS A W;JAMS W R .Two package waterborne urethane systen[J].Progress in Organic Coatings,2002,445:161-183. |
| [8] | 孙哲,李贵贤,王刚,华茂堂,王成.水分散封闭型多异氰酸酯的合成[J].涂料工业,2008(01):34-36. |
| [9] | 李绍雄;刘益军.聚氨酯胶粘剂[M].北京:化学工业出版社,1998:401-402. |
| [10] | 黄志虹,张敬伟,张黎明.二羟基丙酸对聚氨酯复合乳液合成及性能影响[J].皮革科学与工程,2006(04):13-17. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%