Preparation and Properties of Heat-Yellowing Resistant Cathodic Electrophoretic Coating

合成了一种带有(噁)唑烷酮结构的全封闭多异氰酸酯,作为电泳涂料的交联剂.采用傅里叶变换红外光谱(FT - IR)、热重分析(TGA)表征了该交联剂的结构与性能.所制备的阴极电泳涂料具有良好的耐热黄变性能,且涂膜外观良好,各项性能指标优异.

[1]	DONALD W;VENKATACHALAM E;GREGORY J M .Electrodepositable coating compositions and their use in a method of cationic electrodeposition[P].US,6017432,2000-01-25.
[2]	JAMES E P .Compositions useful for electrocoating metal substrates and electrodeposition processes using the coatings[P].US,0024703,2012-02-02.
[3]	柯跃虎,杨卓如.电泳涂料的开发进展[J].化工新型材料,2003(01):27-29.
[4]	李田霞,陈存华.阴极电泳涂料的研究进展[J].现代涂料与涂装,2006(08):37-40.
[5]	KI M S;JONG M H;HOON C .Aqueous dispersion of low-temperature curable cationic electrodeposition resin composition and process for preparing the same[P].US,6130274,2000-10-10.
[6]	洪旭辉,李亚锋.氰酸酯/环氧树脂的固化反应历程[J].高分子材料科学与工程,2012(01):105-108.
[7]	朱晶心;曾繁涤 .环氧封端聚(噁)唑烷酮预聚物的合成[J].太原工业大学学报,1996,27(04):61-65.
[8]	胡靖暐,余新利.阴极电泳涂料用新型交联剂的制备[J].涂料工业,2002(07):23-25.
[9]	张彦华 .封闭异氰酸酯的制备及解封闭研究[D].哈尔滨:东北林业大学,2006.
[10]	KORDOMENOS P I;KRESTA J E;FRISCH K C .Thermal stability of isocyanate-based polymers.2.kinetics of The thermal dissociation of model urethane,oxazolidone,and isocyanurate block copolymers[J].Macromolecules,1987,20(09):2077-2083.

上一张下一张

计量

作者相关

文章评分