对粉末装载量对W-Ni-FemIM合金喂料的粘度及力学性能的影响进行了研究,发现喂料粘度随粉末装载量的升高而增大,但不同粉末装载量喂料的应变敏感性因子基本一致,呈现基本相同的假塑性体流变行为.W-Ni-Fe喂料存在一最佳粉末装载量,此时合金力学性能最好,低于或高于这个粉末装载量都使得合金力学性能降低.