研究了细晶Ti-33Al-3Cr-0.5Mo (质量分数) 合金在超塑性变形过程中的位错运动. 透射电镜分析结果表明, 超塑性变形时, 合金中存在大量位错运动, 在晶界附近和晶粒内形成了位错网, 并在晶界上出现位错塞积. 大多数位错是从晶界及α2相粒子处发射出来的. 还发现了动态再结晶现象, 这种动态再结晶是由于位错的低可动性导致位错密度不断升高造成的. 分析认为, 位错运动是TiAl基合金超塑性变形过程的主要协调机理.
参考文献
[1] | Imayev R M;Kaibyshev O A;Salischev G A .[J].Acta Metallurgica Et Materialia,1992,40(03):581. |
[2] | Wajata T et al.[J].ISIJ International,1993,33(08):884. |
[3] | Lee WB.;Mukherjee AK.;Yang HS. .MECHANICAL PROPERTIES AND MICROSTRUCTURAL CHARACTERIZATION OF A SUPERPLASTIC TIAL ALLOY[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,1995(0):733-740. |
[4] | 周科朝.TiAl基合金超塑性变形的力学特征[J].热加工工艺,1998(03):5. |
[5] | Zhou Kechao;Huang Vaiyun;Qu Xuanhui .Superplastic deformation of TiAl based alloy[J].Transactions of Nonferrous Metals Society of China,1998(2):269-272. |
[6] | Koeppe C.;Clemens H.;Schretter P.;Glatz W.;Bartels A. .OPTIMIZING THE PROPERTIES OF TIAL SHEET MATERIAL FOR APPLICATION IN HEAT PROTECTION SHIELDS OR PROPULSION SYSTEMS[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,1995(1/2):182-193. |
[7] | Cheng S C et al.[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1992,23:1509. |
[8] | Mishra R S;Lee W B;Mukherejee A K.[A].,1995:571. |
[9] | Huang Baiyun;He Yuehui;Zhou Kechao et al.[J].Materials Science and Engineering A,1997,239-240:709. |
[10] | 周科朝,黄伯云,曲选辉.超塑性TiAl基合金的显微组织特征[J].稀有金属材料与工程,1998(06):336-339. |
[11] | Zelin M G;Lee W B;Mukherjee A K .[J].Journal of Materials Research,1994,9(10):2476. |
[12] | Astania V V;Kaibyshev O A;Raizova S N .[J].Acta Metallurgica Et Materialia,1994,42(08):2617. |
[13] | Padmanabhan K A;Schlipf J .[J].Materials Science and Engineering,1996,12(05):394. |
[14] | Ball A;Hutchison M M .[J].Journal of Metallurgy,1969,3:1. |
[15] | Zhou Kechao;Huang Baiyun;Qu Xuanhui .[J].Trans Nonferrous Met Soc China,1998,8(03):437. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%