研究了1100~1250℃温度范围铼在镍(γ) 中的扩散行为.用电子探针测定了扩散偶(Ni-1% Re/Ni-5% Re) 在不同温度下扩散后的成分分布曲线.用 Hall 方法计算出铼在镍(γ)中扩散系数,扩散系数与温度的关系如下:D=5.96×10-1exp{-412(kJ/mol)/RT},在 1100~1200℃的温度范围内,Re 在 Ni中扩散缓慢,而在1200℃以上时,Re的扩散速度明显增加.对Re在 Ni中扩散机制进行了探讨.
参考文献
[1] | Blavette D;Caron P;Khan T .[Z].Superalloys, TMS,1988. |
[2] | Erickson G L .[Z].Superalloys,TMS,1996. |
[3] | Burkholder P S;Thomas M C;Frasier D J.[A].Newcastle upon Type,U.K,1995 |
[4] | Giamei A F;Anton D L .[J].Mata Trans,1985,16A:1997. |
[5] | Hall J D .[J].Journal of Chemical Physics,1953,21:87. |
[6] | Minamino Y;Jung S B;Yamane T .[J].Metallurgical and Materials Transactions,1992,23A:2783. |
[7] | Shimotomai M;Wang T M;Doyama M .[J].Journal of Nuclear Materials,1983,116:347. |
[8] | Shouichi O chiai;Yoshihiro Oya;Tomoo Suzuki .[J].Acta Metallurgy,1984,32(02):289. |
[9] | JUNG S B;Minamino Y;Yamane T.Abstract for the Spring Meeting of the Japan[C].Institute of Metals,1990:94. |
[10] | Monma K;Suto H;Oikawa H J .[J].Journal of the Japan Institute of Metals,1964,28:188. |
[11] | Hirano K;Agarwara R P;Averbach B L et al.[J].Journal of Applied Physics,1962,33:3049. |
[12] | Yamane T;Hisayuki K .[J].The Journal of Microcolumn Separations,1999,34:1835. |
[13] | Walston W S;Schaeffer J C;Murphy W H .[Z].Superalloys,1996. |
[14] | Pollock T M;Murphy W H;Goldman E H et al.[Z].Superalloys,1992. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%