利用数值模拟方法模拟了在喷射成形 Al-Fe-V-Si 系耐热铝合金过程中雾化液滴的飞行状态及凝固行为,给出了不同尺寸雾化液滴的冷却速度和固相分数随飞行距离的变化规律,并对雾化颗粒的形貌组织进行了观察分析.在雾化颗粒中观察到了尺寸在 1～10μm 的第二相,能谱及 XRD 分析表明这种第二相为 Al12(Fe,V)3Si 相.
参考文献
| [1] | Wang W .[J].Journal of Metals,1993,45:16. |
| [2] | Close C M W;Fores F H .[J].Journal of Metals,1994,46:28. |
| [3] | Go B C;Wilshire B .[J].Scripta Metallurgica et Materialia,1992,26:435. |
| [4] | Kim N J .[J].International Journal of Rapid Solidification,1991,6:175. |
| [5] | Rodriguez M A;Skinner D J.[J].Journal of Materials Science,1990(09):1292. |
| [6] | Munson D J .[J].Institute Met,1967,95:217. |
| [7] | Skinner D J;Bye R D;Raybold D et al.[J].Scripta Metallurgica et Materialia,1986,20:867. |
| [8] | Rylands L M;Wikes D M J;Rainforth W M et al.[J].Journal of Materials Science,1994,29:1895. |
| [9] | WANG J Q;Tseng M K;CHEN X F .[J].Materials Science and Engineering,1994,179-180A:412. |
| [10] | Singer A R E .[J].Journal of Met Mater,1970,4:246. |
| [11] | 熊柏青.喷射成形技术的产业化现状及应用发展方向[J].稀有金属,1999(06):425-430. |
| [12] | Gutierrez-Miravete E;Lavernia E J;Tarpaga G M et al.[J].Metallurgical and Materials Transactions,1989,20A:71. |
| [13] | GrantPS;Cantor B;Katgerman L .[J].冶金材料学报,1993,41(11):3097. |
| [14] | Lee Eon-Sik;Ahn S .[J].冶金材料学报,1994,42(09):3231. |
| [15] | 熊柏青;张永安;石力开 .[J].金属学报,1999,35(02):175. |
| [16] | Srivastava A K;Ojha S N;Ranganathan S .[J].Metallurgical and Materials Transactions,1998,29A:2205. |
| [17] | 张家荣;赵廷元.工程常用物质的热物理性质手册[M].北京:新时代出版社,1987:260. |
| [18] | Hariprasad S;Sastry S M L;K L Jerina .[J].Metallurgical and Materials Transactions,1993,24A:865. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%