稀土氧化物(La2O3、Y2O3) 在强化钼的同时,对钼具有显著的韧化作用,即具有综合强韧化作用.稀土钼材作为高温结构材料正逐步取代 Al-Si-K 掺杂钼(ASK)和TZM钼合金;通过成分设计和加工工艺优化,稀土钼还是一种工作温度低、无放射性污染的新型阴极材料,由稀土钼作为阴极的电子管,发射性能与寿命均达到或超过同类型 W-ThO2 阴极电子管,达到实用化水平.因此,稀土钼作为一种集结构与功能于一身的新型材料,有广泛的应用前景.
参考文献
[1] | Linke J .Proceedings of 12th Intern-Plansee Seminar[J].Rutte:Metallwerk Plansee,1989,1:975. |
[2] | Falbriard P .[J].RM & HM,1991,10(01):37. |
[3] | ENDO M .Proeedings of 12th Intern-Plansee Seminar[J].Rutte:Metallwerk Plansee,1989,1:37. |
[4] | Eck R .Proeedings of 12th Intern-Plansee Seminar[J].Rutte:Metallwerk Plansee,1989,1:1047. |
[5] | Zhou M L;Cheng Z C;Zhang J X et al.Proceedings of 13th Inten-Plansee Seminar[J].Rutte:Metallwerk Plansee,1993,1:607. |
[6] | Zhou M L;Li J;Zuo T Y .[J].Transactions Nonferrous Metals Society of China,1994,4(03):57. |
[7] | Zhang J X;Zhou M L;Zuo T Y .Proceedings of 13th Inten-Plansee Seminar[J].Rutte:Metallwerk Plansee,1993,1:599. |
[8] | Zhang J X;Zhou M L;Zuo T Y .Proceedings of 13th Inten-Plansee Seminar[J].Rutte:Metallwerk Plansee,1993,1:93. |
[9] | Leichtfied G .Metal Powder Industries Federation[Z].Prinecton N J,1992. |
[10] | Zhang J X;Zhou M L;Liu D M et al.[J].金属学报(英文版),1996,9(02):94. |
[11] | Zhou M L;Zhang J X;Cheng Z C et al.[J].High Temperature and High Pressure,1994,26:145. |
[12] | 王金淑;周美玲;聂祚仁 等.[J].稀有金属材料与工程,1998,27(ZK):159. |
[13] | Wang J S;Zhou M L;Nie Z R et al.[J].金属学报(英文版),1999,13(04):602. |
[14] | 王金淑,周美玲,张久兴,聂祚仁,左铁镛.碳化La2O3-Mo阴极材料的高温XPS研究[J].稀有金属材料与工程,2000(04):225-227. |
[15] | 王金淑,周美玲,张久兴,聂祚仁,左铁镛.Mo-La2O3阴极La2O3表面富集研究[J].稀有金属材料与工程,2000(05):324-327. |
[16] | Wang J S;Zhou M L;Zhang J X .[J].Transactions Nonferrous Metals Society of China,2001,11(01):25. |
[17] | Wang J S;Zhou M L;Zhang J X .[J].Transactions Nonferrous Metals Society of China,2000,10(06):745. |
[18] | Wang J S;Zhou M L;Zhang J X .[J].Transactions Nonferrous Metals Society of China,2000,10(05):576. |
[19] | Wang J S;Zhou M L;Zhang J X et al.[J].Journal of Alloys and Compounds,2000,311:82. |
[20] | 王金淑,聂祚仁,周美玲,张久兴,胡延槽,左铁镛.La2O3-Mo阴极材料中La2O3稳定性研究[J].稀土,2000(06):18-21. |
[21] | 王金淑,周美玲,张久兴,姚草根,聂祚仁,左铁镛.La2O3-Mo阴极表面碳化层作用机制研究[J].金属学报,2000(11):1205-1208. |
[22] | Wang J S;Zhou M L;Wang Y M et al.Internation Vacuum Electron Sources Conference[R].Orlando, Florida, USA(oral report,2000. |
[23] | Zhang J X;Liu L;Zhou M L et al.[J].RM & HM,1999,17:405. |
[24] | Chen D L;Weiss B;Sticker R et al.Proceedings of 13th Internation Plansee Seminar ′93[J].Rutte Tirol Austria,1993,1:621. |
[25] | 王惠芳;俞淑延 .[J].粉末冶金技术,1990,8(02):75. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%