采用喷射成形技术制备了Al10Zn2.9Mg1.7Cu高强高韧铝合金沉积坯件, 研究了喷射成形制备过程中各工艺参数对沉积坯件的成形性、显微组织、致密度的影响, 确定了适当的工艺参数, 研究了沉积坯件的热挤压及热处理工艺, 对材料的组织进行了分析并对不同状态的材料性能进行了比较. 研究结果表明: 当喷射成形工艺参数合理时, 沉积坯件具有良好的成形性与致密度, 在随后的热挤压过程中, 通过较低的挤压比即可使材料达到全致密; 通过对合金进行适当的热处理, 材料的极限抗拉强度达到810 MPa, 同时延伸率保持在8%～11%, 该材料是一种理想的轻质高强结构材料.
参考文献
| [1] | Lukasak DA;Hart R M .Strong aluminum alloy shave airframe weight[J].Current Advances in Materials and Processes,1991,10:46. |
| [2] | Fridlyander I N .Russian aluminum alloys for Aerospace and transport applications[J].Materials Science Forum,2000,331-337:921. |
| [3] | Schaffer G B;Huo S H .On development of sintered 7XXX series aluminum alloys[J].Powder Metallurgy,1999,42(03):219. |
| [4] | Srivatsan T. S. .Temperature and the Ductility, Deformation, and Fracture of Al 7055[J].JOM,1999(1):0-0. |
| [5] | LEATHAM A G.Spray forming: alloys, products, and markets[A].Baltimore, USA,1999 |
| [6] | Lengsfeld P;Juarez J A;LAVERNIA E J et al.Microstructure and mechanical behavior of spray deposited Zn modified 7XXX Al alloys[J].International Journal of Rapid Solidification,1995,8:237. |
| [7] | 王祝堂;田荣璋.铝合金及其加工手册[M].长沙:中南大学出版社,2000 |
| [8] | 韦强,熊柏青,张永安,朱宝宏,石力开,ZHU Bao-hong,SHI Li-kai.Production of high strength Al-Zn-Mg-Cu alloys |
| [9] | 祝铭亮,周铁涛,刘培英,张永安,熊柏青,石力开,张济山,陈昌麒.最初形成的喷射沉积Al-Zn-Mg-Cu铝合金的显微组织分析[J].稀有金属,2003(04):455-458. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%