研究了第二相对Ti-25V-15Cr-2Al-0.2C-x (x=0, 2% Mo, 2% Nb, 0.2% Si)阻燃β钛合金拉伸断裂行为的影响. 结果表明, β晶界上析出的α相增加了合金发生沿晶断裂的趋势, 特别是热暴露后形成的连续晶界α膜是导致合金脆性沿晶断裂的主要原因. 虽然粗大的碳化物颗粒是合金中的裂纹源之一, 但细小、弥散分布的碳化物却能显著降低合金发生脆性沿晶断裂的趋势, 其原因是细化了β晶粒和有效抑制了晶界α沉淀的析出.
参考文献
| [1] | Seagle S R .The state ofThe USATitanium industry in 1995[J].Materials Science and Engineering,1996,A213:1. |
| [2] | Boyer R R .An overview on the use of titanium in the aerospace industry[J].Materials Science and Engineering,1996,A213:103. |
| [3] | 赵永庆,曲恒磊,朱康英,吴欢,刘彩利,周廉.β型Ti40阻燃钛合金高温长期作用的第二相及其对性能的影响[J].稀有金属材料与工程,2002(02):84-88. |
| [4] | Li Y G;Blenkinsop P A;LORETTO M H et al.Effect of carbon and oxygen on microstructure and mechanical properties of Ti-25V-15Cr-2Al alloy[J].Acta Materialia,1999,47(10):2889. |
| [5] | Li Y G;Blenkinsop P A;LORETTO M H et al.Structure andStability of precipitates in 500 ℃ exposed Ti-25V-15Cr-xAl alloys[J].Acta Materialia,1999,46(16):5777. |
| [6] | Li Y G;Loretto M H;Rugg D et al.Effect of heat treatment and exposure on microstructure and mechanical properties of Ti-25V-15Cr-2Al-0.2C alloy[J].Acta Materialia,2001,49 |
| [7] | 雷力明,黄旭,孙福生,曹春晓,D.Rugg,W.Voice.Ti-25V-15Cr-2Al-0.2C合金的组织、性能及其变形机制[J].中国有色金属学报,2003(04):939-943. |
| [8] | 雷力明,黄旭,孙福生,曹春晓,Rugg D,Voice W.热暴露对Ti-25V-15Cr-2Al-0.2C合金微观组织的影响[J].稀有金属,2003(01):207-209. |
| [9] | 雷力明,黄旭,孙福生,王宝,赵红霞,曹春晓.热处理对Ti-25V-15Cr-2Al-2Mo-0.2C合金组织稳定性的影响[J].稀有金属,2003(04):503-506. |
| [10] | 雷力明 .低成本β稳定型阻燃钛合金的微观组织和力学性能研究[D].北京航空材料研究院,2001. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%