研究变形态Mg-2.5Nd-0.5Zn-0.5Zr合金的超塑变形行为发现, 375 ℃是该合金的最佳超塑变形温度, 变形速率在1×10-2 s-1时延伸率达到329%; 当变形速率提高到2×10-2 s-1时, 该合金的延伸率仍可达到213%. 分析不同真应变下的组织发现, 晶粒在变形初期发生动态再结晶, 晶粒得到破碎而变得细小, 随着变形程度的增加, 晶粒长大程度较小.
参考文献
[1] | Kojima Y .Project of thePlatform science and technology for advanced magnesium alloys[J].Materials Transactions,42(07):1154. |
[2] | Mohri T;Mabuchi M;Nakamura N et al.Microstructure evolution and superplasticity of rolledMg-9Al-1Zn[J].Materials Science and Engineering,2000,290:139. |
[3] | Watanabe H;Mukai T;Mabuchi M;Higashi K .High-strain-rate superplasticity at low temperature in a ZK61 magnesium alloy produced by powder metallurgy.[J].Scripta materialia,1999(2):209-213. |
[4] | Watanabe H;Mukai T;Ishikawa K .High-strain-rate superplasticity in AZ91 alloy processeed by ingot metallurgy[J].Materials Transactions,2002,43(01):78. |
[5] | Langdon T G;Furukawa M;Horita Z et al.Recent development in high strainRate superplasticity[J].Journal of Materials,1998,50(06):41. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%