利用循环伏安法和恒电位电解法探讨了353 K时乙酰胺-尿素(26.7%, 质量分数)-NaBr(12.0%, 质量分数)熔体体系中Gd-Co合金膜的电化学制备.研究了沉积时的电流密度、时间、温度以及Gd(Ⅲ)/Co(Ⅱ)浓度比对沉积膜质量的影响.结果表明, 在乙酰胺-尿素(26.7%)-NaBr(12.0%)熔体中, 控制恰当的体系组成和沉积条件, 均可得到表面均匀、附着力强、有金属光泽的灰黑色非晶态Gd-Co合金膜, 其中Gd的质量分数可达4.92%～85.89%, 所得到的沉积膜通过SEM, EDS 和 XRD进行了分析.
参考文献
| [1] | Chartouni D;Kuriyama N;Kiyokayashi T et al.Air-metal hydride secondary battery with long cycle life[J].Journal of Alloys and Compounds,2002,330-332:766. |
| [2] | Smelling J P;Carey R;Newman D M et al.Thickness variation of the magneto-optical properties of Tb, Dy-Fe Co Pr thin film in urea-NaBr melt[J].Thin Solid Films,1995,259:75. |
| [3] | Yang Q Q;Liu G K;Ao Y B .Electrochemical study on reduction of Gd(Ⅲ) in molten chlorides[J].Molten Salts,1994,14:498. |
| [4] | 杨绮琴 .电化学方法制备稀土材料及稀土在电化学中的应用[J].电化学,1997,3(02):117. |
| [5] | Liu Lizhi,Tong Yexiang,Yang Qiqin.Electroreduction of Co(Ⅱ),Ni(Ⅱ) and Co-deposition with La(Ⅲ) in urea-NaBr Melt[J].稀有金属（英文版）,2000(03):237-241. |
| [6] | Tong Y X;Liu L Z;Xu C W et al.Prearation of Gd-Ni alloy film in urea-NaBr melt[J].中国有色金属学会会刊(英文版),2001,11(03):451. |
| [7] | 徐常威,袁定胜,童叶翔,刘冠昆,沙励嫦.酰胺低温熔盐中Y-Ni合金薄膜的电化学制备[J].中山大学学报(自然科学版),2001(04):127-128. |
| [8] | 王建朝,徐常威,童叶翔,刘冠昆.乙酰胺-尿素-NaBr熔体中Tb-Ni薄膜合金的制备[J].中山大学学报(自然科学版),2002(01):119-120,122. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%