分别用TiCl4,Ti(SO4)2和Ti(OC4H9)4为原料制备纳米二氧化钛粉体.用XRD和TEM对纳米二氧化钛粉体的晶型及晶粒形貌进行了分析.研究了在同一条件下制备的3种纳米二氧化钛粉体对光催化降解亚甲基蓝溶液的影响;结果表明:在相同的制备条件下,用TiCl4为原料制备的纳米二氧化钛晶型较易控制,容易得到含有一定金红石相、催化活性较高的混合晶型的纳米二氧化钛;因此,其降解效果优于其他两种.同时研究了外界条件(如分散剂、干燥方式、温度及烧结温度等)对纳米二氧化钛晶相及其含量变化的影响.实验结果为:用异丙醇做分散剂时,当分散剂与水的体积比为3时,选用冷冻干燥法可得到均分散的粒度可控的球形纳米二氧化钛晶粒.
参考文献
| [1] | MICHELI A L .Fabrication and performance evaluation of a titania automolive exhaust gas sensor[J].American Ceramic Society Bulletin,1984,63(05):694. |
| [2] | Harris L A .Thin palladium films on silicon and titanium[J].Journal of the Electrochemical Society,1982,129(12):2689. |
| [3] | 张力,何芬.TiO2纳米晶材料的制备和光催化性能研究[J].稀有金属,2002(06):441-443. |
| [4] | Zeltner W A;Hill CG;Anderson M A .Supported titania for photodegradation[J].CHEMTECH,1993,23(05):21. |
| [5] | Xianzhi Fu;Walter A. Zeltner;Marc A. Anderson .The gas-phase photocatalytic mineralization of benzene on porous titania-based catalysts[J].Applied Catalysis, B. Environmental: An International Journal Devoted to Catalytic Science and Its Applications,1995(3):209-224. |
| [6] | Bach U.;Lupo D.;Comte P.;Moser JE.;Weissortel F.;Salbeck J. .Solid-state dye-sensitized mesoporous TiO2 solar cells with highphoton-to-electron conversion efficiencies[J].Nature,1998(6702):583-585. |
| [7] | WU Qide,CHENG Bei,ZHANG Gaoke.Preparation of TiO2 nanometer thin films with high photocatalytic activity by reverse micellar method[J].稀有金属(英文版),2003(02):150-154. |
| [8] | 张青红,高濂,郭景坤.四氯化钛水解法制备二氧化钛纳米晶的影响因素[J].无机材料学报,2000(06):992-998. |
| [9] | 李国华,王大伟,徐铸德.纳米二氧化钛粉体晶相控制实验研究[J].无机材料学报,2002(03):422-428. |
| [10] | 张青红,高濂,孙静.煅烧温度对二氧化钛纳米晶性能的影响[J].无机材料学报,2001(05):833-838. |
| [11] | 高伟,吴凤清,罗臻,富菊霞,王德军,徐宝琨.TiO2晶型与光催化活性关系的研究[J].高等学校化学学报,2001(04):660-662. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%