评述了液相法间接制备α-Al2O3粉体过程中,氧化铝前驱体特性和煅烧工艺对α-Al2O3粉体形貌的影响及其控制方法.根据目前在控制氧化铝前驱体形貌方面取得的进展和前驱体转化为α-Al2O3后较难保持其形状的不足,对α-Al2O3粉体形貌控制的研究与开发提出了建议.
参考文献
| [1] | Yashimura M;Kikugawa S;Somiya S .Preparation of alpha alumina fine powders by hydrothermal oxidation method[J].Journal of the Japan Society of Powder and Powder Metallurgy,1983,30(05):207. |
| [2] | Adair J;ChoS;BeliN;etal .Recent developments in morphological control of α-Al2O3 particles synthesized in 1,4-Butanediol solution[J].Journal of Dispersion Science and Technology,2001,22(2-3):143. |
| [3] | 王晶;邱竹贤;谢朋 等.有机醇盐Sol-Gel法纳米氧化铝粉体制备及表征[J].有色金属,1999,51(03):76. |
| [4] | Yu Z Q;Zhao Q;Zhang Q X .Effect of hydrochloric acid on the preparation and characteristics of ultrafine alumina powder[J].Journal of Materials Science Letters,1995,14:531. |
| [5] | 况秀猛 .水热法制备异形超细氧化铝粉末的研究[D].中国科学院化工冶金研究所,1994. |
| [6] | Ogihara T;Nakujina H;Yanagawa T et al.Preparation of monodisperse, spherical alumina powders from alkoxides[J].Journal of the American Ceramic Society,1991,74(09):2263. |
| [7] | Nagai H;Hokazono S;Kato A .Synthesis of aluminium hydroxide by a homogeneous precipitation method I. effect of additives on the morphology of aluminium hydroxide[J].British Ceramic Transactions,1991,90(01):44. |
| [8] | Catone D L;Matijevic E .Aluminum hydrous oxide sols Ⅱ.preparation of uniform spherical particles by hydrolysis of Al secbutoxide[J].Journal of Colloid and Interface Science,1974,48(02):291. |
| [9] | Matijevic E .Preparation and properties of monodispersed colloidal metal hydrous oxides[J].Pure and Applied Chemistry,1978,50:1193. |
| [10] | 施剑林;高建华;阮美玲 .均相沉淀法制备球形氢氧化铝颗粒及其热分解行为[J].无机材料学报,1992,7(02):161. |
| [11] | 宁桂玲;林源;吕秉玲 等.醇盐水解制备Al2O3纳米粉的先驱物体系及控制工艺研究[J].大连理工大学学报,1999,37(03):269. |
| [12] | 谢玉群;陈林深 .纤维状氧化铝粉末的制备[J].材料研究学报,1993,13(03):328. |
| [13] | Ramanathan S;Roy S K;Bhat R et al.Alumina powders from aluminium nitrate-urea and aluminium sulphate-urea reactions-the role of the precursor anion and process conditions on characteristics[J].Ceramics International,1997,23(01):45. |
| [14] | Ramanathan S;Roy S K;Bhat R et al.Preparation and characterisation boehmite precursor and sinterable alumina powders from aqueous aluminium chloride-urea reactions[J].Journal of Alloys and Compounds,1996,243(1-2):39. |
| [15] | Ma H W;Krell A .Synthesis and processing of nano-α-Al2O3powders[J].Key Engineering Materials,2002,206-213:43. |
| [16] | Xue L A;Chen I W .Influence of additives on the γ-to-α transformation of alumina[J].Journal of Materials Science Letters,1992,11:443. |
| [17] | Li J. G.;Sun X. .SYNTHESIS AND SINTERING BEHAVIOR OF A NANOCRYSTALLINE #alpha#-ALUMINA POWDER[J].Acta materialia,2000(12):3103-3112. |
| [18] | Wu Y Q;Zhang Y F;Huang X X et al.Preparation of platelike nano alpha alumina particles[J].Ceramics International,2001,27:265. |
| [19] | Oh CS.;Lee MH.;Choi SC.;Tomandl G. .THE EFFECT OF AN ADDED SEED ON THE PHASE TRANSFORMATION AND THE POWDER PROPERTIES IN THE FABRICATION OF AL2O3 POWDER BY THE SOL-GEL PROCESS[J].Journal of Materials Science,1996(20):5321-5325. |
| [20] | Ceresa E M;Gennaro A;Cortesi P .Alpha-alumina in the form of spherical non-aggregated particles having a narrow size distribution and sizes below 2 microns and process for preparing same[P].US 4818515,1989. |
| [21] | Iga T.;Murase Y. .PREPARATION OF ACICULAR PARTICLES OF ALPHA-ALUMINA[J].Journal of Materials Research,1995(7):1579-1581. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%