分析了钛酸锶(SrTiO3)的晶体结构和性能,利用自蔓延高温合成反应生成钛酸锶(SrTiO3),使Sr2+直接参与合成反应,从根本上解决了S,+包容量的问题.通过多种现代分析技术研究了钛酸锶固化体的物理、化学性能.结果表明固化体样品密度高、孔隙率小、浸出率低且稳定性高,技术和经济上可行.表明自蔓延高温技术制备的钛酸锶是固化锶核素的理想固化体.
参考文献
[1] | Koch L .Minor actinide transmution-a waste management option[J].Journal of the Less-Common Metals,1986,122:371. |
[2] | 罗上庚 .高放废液的分离和嬗变[J].辐射防护,1996,16(01):72. |
[3] | 张玉山.长寿命核废物嬗变处理的研究综述[J].核物理动态,1997(04):251. |
[4] | Ringwood A E;Kesson S E;Ware N G et al.Immoblisation of high level nuclear reactor wastes in SYNROC[J].Nature,1979,278(15):219. |
[5] | Inoue T;Sakata M;Miyashiro H et al.Drvelopment partitioning and transmutation technology for long-lived nuclides[J].Nuclear Technology,1991,93:206. |
[6] | Muthuraman M;Arul Dhas N;Patil K C .Commbustion synthesis of oxide materials for nuclear waste immobilization[J].Bulletin of Materials Science,1994,17(06):977. |
[7] | Borovinskaya I P;Barinova T V;Ratnikov V I et al.Consolidation of radioactives waste into mineral-like material by the SHS method[J].International SHS,1998,7(01):129. |
[8] | T.V.-Barinova;I.P. Borovinskaya;V.I. Ratnikov .SHS Immobilization of Radioactive Wastes[J].Key engineering materials,2002(217):193-200. |
[9] | 郭革新,何文辰,周国香,王爱坤.反铁畸变中钛酸锶(SrTiO3)晶体学原胞的选取[J].河北工业大学学报,2003(01):31-33. |
[10] | 吴庆,赵斌元,胡克鳌.钙钛矿型钛酸锶的制备、结构与性能[J].化工新型材料,2002(08):17-19,5. |
[11] | 罗上庚.回归自然--人造岩石固化放射性废物[J].自然杂志,1998(02):87-90,封3. |
[12] | Standard test method relative to durability of nuclear waste glasses: the product consistency test (PCT) version[S].USA,1991-10-30. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%