研究了包括凝固速率、冷变形和中间热处理对Cu-10Ag合金原位复合材料结构与性能的影响. 观察了铸态组织及其在冷变形和中间热处理后的变化, 测量了材料的极限拉伸强度(UTS)与导电率. 观察到了两阶段应变强化效应, 讨论了影响强度与导电率的因素. 冷却速率在10～103 K·s-1范围内的凝固条件和中间热处理明显影响Cu-10Ag合金原位复合材料的结构与性能.
参考文献
| [1] | Sakai Y.;Inoue K. .Development of a high strength, high conductivity copper-silver alloy for pulsed magnets[J].IEEE Transactions on Magnetics,1992(1):888-891. |
| [2] | 宁远涛,张晓辉,秦国义,张婕.不同凝固条件制备的Cu-Ag合金原位纤维复合材料的结构与性质[J].贵金属,2005(03):39-50. |
| [3] | S.I.Hong;M.A.Hill .Microstructural stability and mechanical response of Cu-Ag microcomposite wires[J].Acta materialia,1998(12):4111-4122. |
| [4] | Hong, SI;Hill, MA .Mechanical stability and electrical conductivity of Cu-Ag filamentary microcomposites[J].Materials Science & Engineering. A, Structural Materials: Properties, Microstructure and Processing,1999(1-2):151-158. |
| [5] | Han K;Vasquez A A;Xin Y et al.Microstructure and tensile properties of nanostructured Cu-25%Ag[J].Acta Materialia,2003,51:767. |
| [6] | A.BENGHALEM;D.G.MORRIS .MICROSTRUCTURE AND STRENGTH OF WIRE-DRAWN Cu-Ag FILAMENTARY COMPOSITES[J].Acta materialia,1997(1):379-406. |
| [7] | JONES H .The status of rapid solidification of alloy in research and application[J].Journal of Materials Science,1984,19(04):1043. |
| [8] | Frommeyer G;Wassenmann G .Microstructure and anomalous mechanical properties of in situ produced silver-copper composite wire[J].Acta Materialia,1975,23:1353. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%