测试了电沉积溶液温度和阴极电流密度变化时电沉积铁箔的磁滞回线.通过铁箔的金相组织观察,电沉积过程的电化学行为及铁箔的EDAX分析,探对了电沉积工艺参数对铁箔磁性能影响的内在原因.结果表明:阴极电流密度增大时,电成型铁箔的矫顽力增大,最大磁导率降低;电沉积溶液温度提高时,铁箔的矫顽力降低,磁导率增大;在650℃经过真空退火后的铁箔矫顽力降低,最大磁导率提高.
参考文献
| [1] | Mcgeough J A;Thomson J R.Some effects of electrolyte flow in the electroforming of iron foil[A].Mechanical Engineering Science Part C,1986:111. |
| [2] | Li D Y;Szpunar J A .Texture formation mechanism during electrodeposition[J].Journal of Materials Science,1993,28(20):5554. |
| [3] | Jean-Crahay;Nicole Lambert;Mario Economopoulos .Elofoil, a new process for the production of iron foil[J].Metallurgical Plant and Technology International,1995(3):72-74,76-0. |
| [4] | 郭占成,刘宇星,刘美凤,卢维昌.电沉积Fe、Ni基合金箔的组织形貌及磁性能[J].中国有色金属学报,2004(02):273-279. |
| [5] | 姜力强,郑精武,陈巧玲.电沉积软磁铁箔连续化生产的关键技术研究[J].稀有金属,2005(03):293-296. |
| [6] | 田民波.磁性材料[M].北京:清华大学出版社,2000 |
| [7] | Vitkin A I;Paramonov V A;Filatova N G .Technology of thin ferrum production by electrolytic method[J].Stal,1991,2:79. |
| [8] | 李腾,陈敏勤,金瑞湘,李卫.热处理对高矫顽力型FeCrCo合金性能的影响[J].稀有金属,2003(05):558-560. |
| [9] | 陈国均;李茂昌;周元龙.金属软磁材料及其热处理[M].北京:机械工业出版社,1986:175. |
| [10] | 艾柳庭;郭建本;王天旭 等.热处理工艺对电铸电工纯铁性能的影响[J].钢铁,1996,31(08):50. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%