探讨了CTAB/n-C4H9OH/c-C6H12/H2O体系微乳液的稳定性,绘制了该体系的三元和拟三元相图,当CTAB与n-C4H9OH质量比为2:3时有较宽的稳定的W/O微乳液相区,是制备超细Y2O3的理想体系.在该体系稳定区内,通过调整ω,可改变微乳水核半径.Y(NO3)3溶液和草酸溶液在微乳液水核(微反应器)中进行沉淀反应,制备出不同粒径、形貌的超细氧化钇.样品经X射线衍射(XRD)、透射电镜(TEM)表征,结果表明,ω增大,水核半径增大,超细Y2O3的粒径变小,形貌也发生变化.当ω=17时,可制备出粒径为30 nm的晶型完好的Y2O3立方晶粒.
参考文献
| [1] | Adolph L;Dennis F .High-density yttria for particle ceramic application[J].Journal of the American Ceramic Society,1992,73(03):709. |
| [2] | 李强,高濂,严东生.纳米Y2O3：Eu3+粉体的表面包膜处理[J].无机材料学报,1999(01):150-154. |
| [3] | Daniel S;Mufit A .Preparation of spherical,monosized Y2O3 precursor particles[J].Journal of Colloid and Interface Science,1998,122(01):47. |
| [4] | 向柠,陈洪龄,徐南平.超细氧化钇粉体的制备[J].高校化学工程学报,2002(01):48-52. |
| [5] | Hussein G A M .Formation of high surface-area yttrium oxide by the thermal decomposition of different inorganic precursors[J].Thermochimica Acta,1994,244:139. |
| [6] | Chhabra V;Pillai V;Mishra B K et al.Synthesis,characterization,and properties of microemulsion-mediated nanophase TiO2 particles[J].Langmuir,1995,11:3307. |
| [7] | Kim Eui Jung;Hahn Sung-Hong .Microstructural changes of microemulsion-mediated TiO2 particles during calcination[J].Materials Letters,2001,49:244. |
| [8] | 催正刚;殷福珊.微乳化技术及应用[M].北京:中国轻工业出版社,1999:407. |
| [9] | 吴宗斌;王丽萍;洪广言 .反相胶束微乳液法制备氧化钇纳米微晶[J].应用化学,1999,16(06):9. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%