研究了Ti-47.5Al-6(Cr,Nb,W,Si,B)%合金在不同试验温度和试验应力下的蠕变性能,并分析了不同试验条件下的蠕变机制.试验结果表明,该合金在760℃,100～150MPa具有良好的蠕变性能,在200MPa,700～800℃温度范围内蠕变激活能为U≈299kJ·mol-1,蠕变机制受原子扩散过程控制.在760℃和100～200MPa应力范围内,蠕变应力指数n从2.1变到4.2,故蠕变变形由高密度界面滑移控制变为位错攀移控制的回复蠕变.
参考文献
| [1] | Hayes R W;McQuay P A .A first report on the creep deformation and damage behavior of a fine grained fully transformed lamellar gamma TiAl alloy[J].Scripta Metallurgica et Materialia,1994,30(02):259. |
| [2] | Bhowal P R;Konkel W A;Merrick H F;Kim Y W,Wagner R,Yamaguchi M.Gamma Titanium Aluminides[M].TMS,Warrendale,PA,1995:787. |
| [3] | Viswanathan G B;Kim Y W;Mills M J;Kim Y W,Dimiduk D M,Loretto M H.Gamma titanium aluminides[M].TMS,Warrendale,PA,1999 |
| [4] | Kim Y M.Gamma TitaniumAluminides[M].Las Vegas:TMS,1999:441. |
| [5] | Nathal M V.Structure Intermetallics[M].Las Vegas:TMS,1997:109. |
| [6] | 李书江,刘自成,林均品,陈国良,张卫军.一种高铌TiAl合金的蠕变性能[J].稀有金属材料与工程,2002(01):31-36. |
| [7] | Kim Y M.Gamma Titanium Aluminides[M].Las Vegas:TMS,1999:985. |
| [8] | Zhu Hanliang;Seo D Y;Maruyama K et al.Effect of microstructural stability on creep behavior of 47XD TiAl alloys with fine-grained fully lamellar structure[J].Scripta Materialia,2005,52:45. |
| [9] | 冯端.金属物理学,第三卷:金属力学性质[M].北京:科学出版社,1999:560. |
| [10] | 陈国良;林均品.有序金属间化合物结构材料物理金属学基础[M].北京:冶金工业出版社,1999:195. |
| [11] | 哈宽福.金属力学姓质的微观理论[M].北京:科学出版社,1983:507. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%