通过zeta电位、红外光谱等研究了用共沉淀方法制备LaCoO3时分散剂-聚乙二醇PEG-4000)的作用机制;通过粘度测定选择其适宜的使用量. 结果表明: 聚乙二醇的防团聚性能是通过在超细粉体的前驱体上吸附, 进而主要通过空间位阻稳定机制发挥作用的. 当其使用量为前驱体质量的3.0%时, 可制备出团聚程度轻、分散性良好的超细LaCoO3粉体.
参考文献
| [1] | Vlaeimir Krivoruchko;Tat′yana Konstantinova;Anton Mazur;Andrey Prokhorov,Victor Waryukhin .Magnetic resonances spectroscopy of nanosize particles La0.7Sr0.3MnO3[J].Journal of Magnetism and Magnetic Materials,2006,300:e122. |
| [2] | 刘源.钙钛矿型LaCOO3和LaMnO3超细粒子的制备[J].内蒙古工业大学学报(自然科学版),2000(03):192-195. |
| [3] | Shu J;Kaliaguine S .Well-dispersed perovskite-type oxidationcatalysts[J].Applied Catalysis B:Environmental,1998,16:303. |
| [4] | Michael W.Lufaso;Hans-Conrad zur Loye .Crystal Structures and Magnetic Properties of Mixed Iridium-Ruthenium Triple Perovskites.1.Ba_3MRuIrO_9(M = Lanthanide,Y)[J].Inorganic Chemistry: A Research Journal that Includes Bioinorganic, Catalytic, Organometallic, Solid-State, and Synthetic Chemistry and Reaction Dynamics,2005(25):9143-9153. |
| [5] | 陈少贞;陈林凤.湿化学法制备ZrO2超细粉的团聚机理、表征及控制[J].材料导报,1996(03):39. |
| [6] | 赵青,常爱民,简家文,巴维真.改性溶胶-凝胶法制备ZrO2纳米粉及其团聚控制[J].材料科学与工程学报,2003(05):683-686. |
| [7] | 中西香尔;索罗曼 P H;王绪明.红外光谱分析100例[M].北京:科学出版社,1984:21. |
| [8] | 刘梅堂,韦园红,史济斌,刘洪来.高分子PVP吸附对胶体Zeta电位的影响[J].中国粉体技术,2001(02):1-4. |
| [9] | 张海军,贾晓林,刘战杰,李文超.纳米Al2O3-SiO2的分散及颗粒间力的相互作用[J].硅酸盐学报,2003(10):928-933,939. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%