介绍了生产加工钛粉最常用的方法--氢化脱氢法.金属钛(粉)在一定温度下便开始与氢气发生剧烈的反应,当含氢量大于2.3%时,产物疏松,易于粉碎成细小颗粒的氢化钛粉,氢化钛粉经过大约700 ℃左右的温度,将其分解以及将钛粉中固溶的大部分氢除去,可得到钛粉.从热力学原理、脱氢曲线,差热分析、平衡分压与氢气的关系等方面对氢化脱氢法做了概要的分析.试验证明,钛中氢的含量随温度的升高逐渐降低,在680 ℃时氢化钛出现吸热峰迅速分解,钛的氢化反应温度区间为350～680 ℃.氢化脱氢法生产的钛粉的杂质主要取决于原料的纯度和杂质情况,严格注意操作中的环节,只会引入少量的氧或碳等杂质.对于相同原料制取的钛粉,粒度越细,其含氧量越高.
参考文献
| [1] | 莫畏;邓国珠;罗方承.钛冶金[M].北京:冶金工业出版社,1998:8. |
| [2] | Okabe T H;Waseda Y .Producing titanium through an electronically mediated reaction[J].Journal of Metals,1997,49(06):28. |
| [3] | Okabe TH.;Sadoway DR. .Metallothermic reduction as an electronically mediated reaction[J].Journal of Materials Research,1998(12):3372-3377. |
| [4] | Steven J. Gerdemann .TITANIUM Process Technologies[J].Advanced Materials & Processes,2001(7):41-43. |
| [5] | Kraft E H.Opportunities for low cost titanium in reduced fuel consumption,improved emissions,and enhanced durability heavy-duty vehicles[M].Washington:EHK Technologies,2002:31. |
| [6] | 王志,袁章福,郭占成.金属钛生产工艺研究进展[J].过程工程学报,2004(01):90-96. |
| [7] | Okabe T H;Oda T;Mitsuda Y .Titanium powder production by preform reduction process(PRP)[J].Journal of Materials Research,2004,364:156. |
| [8] | 王碧侠,兰新哲,赵西成,吴晓松.二氧化钛直接还原制取金属钛的工艺进展[J].稀有金属,2006(05):671-677. |
| [9] | Froes FH;Trindade B .The mechanochemical processing of aerospace metals[J].Journal of Materials Science,2004(16/17):5019-5022. |
| [10] | Froes F H;Eranezhuth B G;Senkov Oleg N .Reduction of metal oxides through mechanochemical processing[P].US 6152982,2000. |
| [11] | Froes F H;Eranezhuth B G;Prisbrey K .Mechanochemical processing for metals and metal alloys[P].US 6231636,2001. |
| [12] | 黄金昌.低成本钛粉末产品的生产、性能和应用[J].稀有金属与硬质合金,2001(04):45-48. |
| [13] | 洪艳;沈化森;王兆林;曲涛 .低成本钛粉生产工艺[J].中国有色金属学报,2005,15(02):343. |
| [14] | 侯德祥.日本用氢化脱氢法生产低氧钛粉技术[J].有色矿冶,1997(02):31-34. |
| [15] | 李光明;甘礼华;陈龙武 .氢化钛的制备及分解[J].应用化学,1998,15(01):77. |
| [16] | Dinsdale A T .Sgte date for pure elements[J].CALPHAD-Computer Coupling of Phase Diagrams and Thermochemistry,1991,15(04):317. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%