对粉末冶金法制备的碳化硅颗粒增强铝基复合材料进行了旋转弯曲疲劳试验研究.采用金相显微镜和扫描电镜分别观察了疲劳试验后复合材料纵向显微组织和疲劳断口.通过金相显微镜,观察了增强体颗粒在疲劳循环应力水平下可能的损伤形式.通过疲劳断口观察,分析了断面上不同区域的疲劳裂纹传播特征.结果表明,增强体的加入有效地提高了复合材料的屈服强度、弹性模量和疲劳性能,使复合材料高周疲劳极限提高到约250 MPa(1×107循环周次).复合材料的疲劳损伤随机分布于试样内.断口分析还表明复合材料疲劳同样遵循裂纹萌生, 长大, 失稳断裂规律,其裂纹起源于铝基体内.加入SiC颗粒减弱或遮盖了疲劳裂纹传播时的晶体学特征,使得复合材料高周疲劳断面没有发现常见的疲劳辉纹.
参考文献
| [1] | Geiger A L;Walker R J A .The processing and properties of discontinuously reinforced alumininum composites[J].Journal of the Minerals Metals & Materials Society,1991,8:8. |
| [2] | Mark Hull .Commercial success for MMCs[J].Powder Metallurgy,1998(1):25-26. |
| [3] | Maruyama B;Hunt W H .Discontinuously reinforced alumininum:current status and future direction[J].Journal of the Minerals Metals & Materials Society,1999,11:59. |
| [4] | Andrew T .Leading edge MMCs and powder materials[J].Powder Metallurgy,1997,40(02):102. |
| [5] | Lioyd D J .Particle reinforced aluminium and magnesium matrix composites[J].International Materials Reviews,1994,39(01):1. |
| [6] | 王祝堂;田荣璋.铝及铝合金加工手册[M].长沙:中南大学出版社,2000 |
| [7] | 崔约贤;王长利.金属断口分析[M].哈尔滨:哈尔滨工业大学出版社,1998 |
| [8] | 哈宽富.金属力学性质的微观理论[M].北京:科学出版社,1983 |
| [9] | Forsyth P J E .Fatigue damage and crack growth in aluminum alloys[J].Acta Metallurgica,1963,11:703. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%