以LiOH, NiO, Co2O3, Ba(OH)2为原料, 利用流变相反应法制备前驱物(优点是反应体积小, 原料混合得比较均匀, 在反应过程中金属元素的原始比例能够保持不变), 然后在空气中灼烧,合成了掺杂钡离子的锂镍钴复合氧化物锂离子电池正极材料. 用ICP-AES,SEM,粉末X射线衍射法表征了该复合氧化物的组成和结构. 用模拟充放电系统,在100 mA·g-1的恒定电流密度下测定其充放电性质, 第二周放电比容量高达192 mAh·g-1, 循环50周后放电比容量还有158 mAh·g-1,容量保持在83%.
参考文献
| [1] | Jaephil C;Geunbae K;Lim H S .Soluble 2,5-dimercapto-1,3,4-thiadia zole/poly (o-toluidine) electroactive composite[J].Journal of the Electrochemical Society,1999,146(10):3571. |
| [2] | Li W;Currie J C .Dimercaptan-polyaniline cathodes for lithium batteries:addition of polypyrrole derivative for rapid charging[J].Journal of the Electrochemical Society,1997,144:2773. |
| [3] | Saadoune I;Delmas C .Electrochemical characteristics of the dimercaptanpoly (ethylene oxide) grafted polyaniline electrodes[J].Journal of Solid State Chemistry,1998,136:8. |
| [4] | ZHU Xianjun,ZHAN Hui,LIU Hanxing,ZHOU Yunhong.Synthesis and characterization of LiNi0.95-xCoxAl0.05O2 for lithium-ion batteries[J].稀有金属（英文版）,2006(04):303-308. |
| [5] | 王昌胤,卢世刚,阚素荣.固相法制备LiNi0.25Co0.5Mn0.25O2正极材料的研究[J].稀有金属,2007(01):77-80. |
| [6] | 杜荣斌.尖晶石材料LiMn2O4的研究现状及展望[J].化工新型材料,2006(02):1-4. |
| [7] | 刘汉三,杨勇,张忠如,林祖赓.锂离子电池正极材料锂镍氧化物研究新进展[J].电化学,2001(02):145-154. |
| [8] | 杜荣斌,刘峥.锂和钴元素掺杂对锂锰尖晶石结构和性能的影响[J].电源技术,2006(09):736-739. |
| [9] | Ying J R;Wang C R;Jiang C Y .Preparation and characterization of high-density LiNi0.8Co0.2O2 cathode material for lithium secondary batteries[J].Journal of Power Sources,2001,99:78. |
| [10] | 高农,王虹,顾大明.锰掺杂LiNi0.8Co0.2O2的合成及电极性能研究[J].电机与控制学报,2005(04):349-351,356. |
| [11] | 李若愚,陈白珍,肖立新,李义兵,李改变,常晓燕.镍钴酸锂的制备与电性能研究[J].有色金属（冶炼部分）,2005(04):40-44. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%