研究了采用传统冶金工艺制备的错基吸气剂在不同激活温度下的吸气性能,对比了锫基吸气剂对H2,N2,CO的吸气性能,同时对吸气剂的孔隙度、孔径、比表面积、表面形貌进行了测试.结果表明,激活温度为500℃时,吸气剂就具有吸气性能,随着激活温度的升高,吸气剂的吸气性能越好;吸气剂对H2的吸气性能远远好于N2和CO.对吸气剂在不同激活温度下吸气性能差异的原因做了深入的探讨,并初步分析了吸气剂对于不同气体的吸收性能,从而使人们对锆基吸气剂的认识更加深入全面.
参考文献
| [1] | Giorgi T A;Ferrario B;Storoy B .An updated review of getters and gettering[J].Journal of Vacuum Science and Technology A,1985,A3(02):417. |
| [2] | 庄寿全.现代吸气材料及其应用技术[J].真空电子技术,1994(05):42. |
| [3] | Benvenuti C;Chiggiato P;Cicoira F;Ruzinovt V .Decreasing surface outgassing by thin film getter cnatings[J].Vacuum,1998,50(1-2):57. |
| [4] | Boffitto C;Doni F;Rosai L J .The propertics of some xirconiumbseed gettering alloys for hydrogen istope storage and purification[J].Less-Commen Metals,1984,104(01):149. |
| [5] | 万玉金.吸气剂[M].南京:江苏科学技术出版社,1983:63. |
| [6] | Borghi M;Ferrario B .Use d nonevaporable getter pumps in experimental fusion reactors[J].Journal of Vacuum Science and Technology,14(01):570. |
| [7] | Ferrario B .Chemical pumping in vacuum technology[J].Vacuum,1996,47(41):363. |
| [8] | Gsspurini G;Ferrario B;Raimondi S .Water vapour sorption characteristics of a non-evapurable getter pump[J].Vacuum,1993,44(06):733. |
| [9] | 邓凤翔;李跃权;张云霞;詹锋 尉秀英 马胜跃 .一种宽激活温度范围的吸气剂和吸气元件[P].CN 85102889,1985. |
| [10] | GB 8763288.GB 8763288.非蒸散型吸气材料及制品吸气性能测试方法[S].,1987. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%