采用累积叠轧焊法制备了Al/AZ31多层复合材料,并通过扫描电镜、X射线能谱仪和显微硬度计对所制备的Al/AZ31多层复合材料进行了横截面形貌观察、能谱分析以及显微硬度测试.结果表明,经过三道次的累积叠轧焊之后可制备Al/AZ31多层复合材料.能谱分析表明,在Al层和AZ31层的界面处产生了扩散层.随着轧制道次的增加扩散层的厚度逐渐增加.显微硬度测试表明,随着轧制道次的增加,Al/AZ31多层复合材料的层组元的强度也随之增加,但Al层的强度较AZ31增加得快,并且形成的界面扩散层具有一定的硬度梯度.
参考文献
[1] | F.H.Kavarana;K.S.Ravichandran .NANOSCALE STEEL-BRASS MULTILAYER LAMINATES MADE BY COLD ROLLING: MICROSTRUCTURE AND TENSILE PROPERTIES[J].Scripta materialia,2000(10):947-954. |
[2] | Y.P. Li;G.P. Zhang;W. Wang;J. Tan;S.J. Zhu .On interface strengthening ability in metallic multilayers[J].Scripta materialia,2007(2):117-120. |
[3] | Alexandre G;Nguyen H H;Nora D;Dominique G .Preparation of microstmctured and nanostrnctured magnetic materials by mechanical deformation[J].Journal of Magnetism and Magnetic Materials,2002,242-245:581. |
[4] | 胡小草,刁训刚,郝雷.大面积柔性基底TiO2/Ag/Ti/TiO2多层膜的制备及其光电和红外发射特性[J].稀有金属,2008(03):300-305. |
[5] | Wadley H N G;Hsiung L M;Lankey R L .Artificially layered nanocomposites fabricated by jet vapor deposition[J].Composites Engineering,1995,5(07):935. |
[6] | NabiRahni D M A;Tang P T;Leisner P .The electrolytic plating of compositionally modulated alloys and laminated metal nanostructures based on an automated computer-controlled dual-bath system[J].NANOTECHNOLOGY,1996,7(02):134. |
[7] | Saito Y.;Tsuji N.;Sakai T.;Utsunomiya H. .Novel ultra-high straining process for bulk materials - Development of the accumulative roll-bonding (ARB) process[J].Acta materialia,1999(2):579-583. |
[8] | P.J. Hsieh;Y.P. Hung;J.C. Huang .Transformation into nanocrystalline or amorphous materials in Zr-X binary systems using ARB route[J].Scripta materialia,2003(2):173-178. |
[9] | S. Ohsaki;S. Kato;N. Tsuji .Bulk mechanical alloying of Cu-Ag and Cu/Zr two-phase microstructures by accumulative roll-bonding process[J].Acta materialia,2007(8):2885-2895. |
[10] | Chen I W;Winn E J;Menon M .Application of deformation instability to microstructural control in muhilayer ceramic composites[J].Materials Science and Engineering A:Structural Materials Properties Microstructure and Processing,2001,317:226. |
[11] | Min G H;Lee J M;Kang S B;Kim H W .Evolution of microstructure for muhilayered Al/Ni composites by accumulative roll bonding process[J].Materials Letters,2006,60(27):3255. |
[12] | Zhang R G;Acoff V L .Processing sheet materials by acumulative roll bonding and reaction annealing from Ti/Al/Nb elemental foils[J].Materials Science and Engineering A:Structural Materials Properties Microstructure and Processing,2007,463:67. |
[13] | 谢华,钱匡武,陈文哲.Ni-P-金刚石化学复合镀层与钢基的扩散[J].金属学报,2001(08):841-844. |
[14] | Seong-Hee Lee;Tetsuo Sakai;Yoshihiro Saito;Hiroshi Utsunomiya;Nobuhiro Tsuji .Strengthening of sheath-rolled aluminum based MMC by the ARB process[J].Materials transactions,1999(12):1422-1428. |
[15] | Lee SH.;Saito Y.;Sakai T.;Utsunomiya H. .Microstructures and mechanical properties of 6061 aluminum alloy processed by accumulative roll-bonding[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2002(1/2):228-235. |
[16] | Yutaka S. Sato;Seung Hwan C. Park;Masato Michiuchi;Hiroyuki Kokawa .Constitutional liquation during dissimilar friction stir welding of Al and Mg alloys[J].Scripta materialia,2004(9):1233-1236. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%