通过在Gleeble1500D热模拟试验机上进行等温热压缩试验,研究了7050高强铝合金在变形温度为300～450℃和应变速率为0.01～10s-1条件下的流变应力变化规律,计算推导出包含Arrhenius项的zener-Hollomon参数描述7050合金高温压缩流变行为的表达式.结果表明:应变速率和变形温度对7050合金的流变应力影响显著,流变应力随温度升高而降低,随应变速率的提高而增大;7050合金属于正应变速率敏感材料,合金的形变激活能为163.7425 KJ·mol-1.
参考文献
| [1] | Mukhopadhyay A K .High strength aluminium alloys for structural application[J].Metals Materials and Processes,2007,119(01):1. |
| [2] | 高凤华,李念奎,丛福官,田妮,赵刚.7050合金半连续铸锭中结晶相及其均匀化处理[J].稀有金属,2008(03):274-278. |
| [3] | Robson J D .Microstructural evolution in aluminium alloy 7050 during processing[J].Materials Science and Engineering A:Structural Materials Properties Microstructure and Processing,2004,382:112. |
| [4] | Shi H;Mclarem A J;Sellars C M;Shahani R Boling Broke R .Constitutive equations for high temperature flow stress of aluminum alloys[J].Journal of Materials Science and Technology,1997,13:210. |
| [5] | 李锡武,熊柏青,张永安,华成,王锋,朱宝宏,熊益民.新型Al-Zn-Mg-Cu合金热变形流变应力特征[J].稀有金属,2008(05):552-557. |
| [6] | Sheppard T;Jackson A .Constitutive equation for use in prediction of flow stress during extrusion of aluminium alloys[J].Journal of Materials Science and Technology,1997,13(03):203. |
| [7] | Sellars C M .Modeling microstructural development during hot rolling[J].Journal of Materials Science and Technology,1990,16(11):1072. |
| [8] | Poirier J P;关德林.晶体的高温塑性变形[M].大连:大连理工大学出版社,1989:24. |
| [9] | 沈键 .2091铝锂合金高温塑性变形行为研究[D].中南工业大学,1996. |
| [10] | 李杰,尹志民,黄继武,王涛.超高强Al-Zn-Mg-Cu-Zr合金的热变形行为[J].稀有金属,2004(01):166-170. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%