采用化学反应共沉淀法制备出金属Al及Y-Al复合掺杂的α-Ni(OH)2粉体样品,采用XRD,TG-FTG,EDS和IR手段对样品的结构进行了表征,并测试了样品作为电极活性材料的电化学性能.结果发现,与掺10%Al样品相比,复合掺杂5%Y和10%Al的α-Ni(OH)2具有更大的层间距,晶格间有较多的结晶水,电极反应具有更好的可逆性和较小的电化学阻抗,样品电极材料组成的MH-Ni电池,在以80 mA·g-1恒电流充电6 h,20 mA·g-1恒电流放电,终止电压为1.0 V的克放电制度下,放电比容量达到388.01 mAh·g-1,同时放电中值电压较高并稳定于1.29 V.
参考文献
| [1] | Comilsen B C;Shan X;Loyselle P L .Structural comparison of nickel electrodes and precursor phases[J].Power Sources,1990,29:453. |
| [2] | ZHANG Qian,XU Yan-hui,WANG Xiao-lin,HE Guo-rong.Effect of preparation conditions on properties of Al-substituted α-Ni(OH)2 prepared by homogeneous precipitation[J].中国有色金属学会会刊（英文版）,2005(03):653-660. |
| [3] | Zhao Y L;WangJ M;Chen H;PanT,ZhangJ Q,Cao C N .Different additives-substituted α-Ni(OH)2 hydroxide prepared by urea decomposition[J].Elcctrechim Acta,2004,50(06):91. |
| [4] | 冷拥军,王凤军,刘兵,廖小珍,孝英,马紫峰.铝取代氢氧化镍制备、结构与电化学性能（Ⅰ）电化学性能[J].电源技术,2000(02):77-80. |
| [5] | 冷拥军,刘兵,王凤军,周锦鑫,孝英,马紫峰.铝取代氢氧化镍制备、结构与电化学性能Ⅱ结构分析[J].电源技术,2000(06):326-329. |
| [6] | 宋莎,刘长久.化学共沉淀法制备铝掺杂α-Ni（OH）2的控制条件[J].广西科学,2008(02):161-165. |
| [7] | 任俊霞,周震,阎杰.Y掺杂对氢氧化镍电极高温性能的影响[J].物理化学学报,2007(05):738-742. |
| [8] | 刘长久,钟胜奎,柴小琴,孙美红.复合掺杂纳米α-Ni（OH）2的制备与性能[J].电池,2004(06):434-435. |
| [9] | Kamath P V;Dixit M;Indira M .Stabilized α-Ni (OH)2 as electrode material of alkaline secondary cells[J].Journal of the Electrochemical Society,1994,141(11):2956. |
| [10] | Watanabe K.;Kumagai N.;Kikuoka T. .PHYSICAL AND ELECTROCHEMICAL CHARACTERISTICS OF NICKEL HYDROXIDE AS A POSITIVE MATERIAL FOR RECHARGEABLE ALKALINE BATTERIES[J].Journal of Applied Electrochemistry,1995(3):219-226. |
| [11] | 常照荣,齐霞,吴锋,苗旺,孙东.高密度非球形β-Ni（OH）2的制备研究[J].稀有金属,2006(03):291-294. |
| [12] | 肖慧明,王建明,陈惠,潘滔,张鉴清.Al取代α-Ni（OH）2 的有机溶剂法合成及其电化学性能[J].功能材料,2003(05):553-555. |
| [13] | 南俊民,唐致远,刘建华,宋全生.Ni（OH）2电极材料的xRD和Raman光谱表征[J].应用化学,2001(02):108-111. |
| [14] | Oliva P;Lconadi J;Lanront J F .Review of the structure and the electrochemistry of nickel hydroxidas and oxy-hydroxides[J].Power Sources,1982,8:229. |
| [15] | 张倩,徐艳辉,王晓琳.Al代α-Ni（OH）2的结构与电化学性能[J].稀有金属材料与工程,2003(10):825-828. |
| [16] | 杨书廷,陈改荣,尹艳红,贾俊华,陈红军,赵培正.掺杂稀土元素对Ni（OH）2晶格的影响[J].电源技术,2002(04):278-280. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%