研究了固溶温度对FeNi32.5Co4Mn0.2Nb0.1超因瓦合金Nbc析出及热膨胀系数的影响,在840,940,1040及1140℃对合金进行40 min的热处理并水淬,随后在300℃退火4 h.TEM观察到合金中存在微米级及纳米级NbC析出物,随着圊溶温度升高NbC含量减少,在1140℃固溶时合金中的NbC完全溶解.随固溶温度从840℃升至1040℃,合金的膨胀系数度减小,在合金经1140℃固溶处理后却显著增加.NbC的析出大幅度降低合金的膨胀系数;通过调整NbC含量,可获得低于0.1×10-6/℃膨胀系数.
参考文献
| [1] | 何开元.精密合金材料学[M].北京:冶金工业出版社,1991:173. |
| [2] | Sokolowsi W;Hsieh C;O'Donnell T .New HP(High Purity) Invar36[P].US 5476633,1995-12-19. |
| [3] | Masaomi;Taniuchi;Toshihiko .Method of producing Fe-Ni series alloys having improved effect for restraining streaks during etching[P].US 5002619,1991-3-26. |
| [4] | Fe-38Ni-Mo-V-C低膨胀合金碳化物析出规律的研究[J].宝钢技术,2005(05):30-33. |
| [5] | 郑鲁;雍岐龙;孙珍宝 .碳化铌在微合金钢中的溶解[J].金属学报,1987,23(06):277. |
| [6] | Lee EH.;Mansur LK. .Fe-15Ni-13Cr austenitic stainless steels for fission and fusion reactor applications. II. Effects of minor elements on precipitate phase stability during thermal aging[J].Journal of Nuclear Materials: Materials Aspects of Fission and Fusion,2000(1):11-19. |
| [7] | 韦青峰.铌微合金化HSLA钢铁素体中Nb（C,N）析出强化的研究进展[J].特殊钢,2007(05):42-44. |
| [8] | 雍岐龙;裴和中;田建国;周晓玲 潘俐 杨文勇 .铌在钢中的物理冶金学基础数据[J].钢铁研究学报,1998,10(02):66. |
| [9] | 钟文定.铁磁学(中)[M].北京:科学出版社,1987:323. |
| [10] | Rajendra U;Vaidya;Chawla K K .Thermal expansion of metalmatrix composites[J].Composites Science and Technology,1994,50(01):13. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%