采用固相反应法制备了掺镝W型钡镍铁氧体粉体.利用X射线衍射仪及扫描电子显微镜对其晶体结构及微观形貌进行分析,使用微波网络分析仪对其微波电磁性能进行研究.结果表明:1350℃时,不同Dy掺杂量下均形成了纯度较高的W型钡镍铁氧体,六角片状结构完整.在15～18 GHz频段:μ",tanμ值随Dy掺杂量的增加而增大,掺镝摩尔分数x=0.08时达到最大.
Ferrite Ba_(1-x)Dy_x Ni_2Fe_(16)O_(27) powders were prepared by solid state method. Phase composition and particle appearance were analyzed with X-ray diffraction (XRD) and scan electron microscope (SEM). Network analyzer was used to study electromagnetic pa-rameters. It was found that powders crystallized into W-type ferrite phase and formed W-type hexagonal plane ferrite at 1350 ℃. In the range from 15 to 18 GHz,μ" and tang increased with the addition of Dy and reached the highest values when doping molar fraction x =0.08.
参考文献
| [1] | 李斌太,陈大明,陈钦生.铁氧体微波吸收材料的研究进展[J].硅酸盐通报,2004(05):66-69. |
| [2] | 康青.新型微波吸收材料[M].北京:科学出版社,2006 |
| [3] | 王文梅,孙传尧.纳米稀土铁氧体磁性颗粒的制备研究[J].稀有金属,2007(01):27-31. |
| [4] | 郭睿倩;李洪桂;孙培梅;李运姣 赵中伟 .轻稀土镧取代M型钡铁氧体超微粉末的合成与表征[J].稀有金属,2001,25(05):86. |
| [5] | 李小靖.锂系铁氧体材料中Nb2O5的微量掺杂[J].稀有金属,2003(05):643-644. |
| [6] | 钱九红.纳米多波段隐身材料研究进展[J].稀有金属,2006(04):511-516. |
| [7] | 徐坚,熊惟皓,曾爱香,王采芳.稀土元素在磁性吸波材料中的应用研究进展[J].稀土,2004(06):68-73. |
| [8] | 刘学东,卢佃清,范喆,徐超.（La0.5Na0.5）xBa1-xFe12O19纳米铁氧体粉末的微波吸收特性[J].磁性材料及器件,2007(01):40-42. |
| [9] | 李红英,施伟光,甘树才.稀土六方Z型铁氧体Ba3-xLaxCo2Fe24O41的合成及电磁性能与吸波特性[J].吉林大学学报（工学版）,2006(06):856-860. |
| [10] | 刘颖,王敬平,胡敏,张密林,夏天.溶胶-凝胶法制备单磁畴M型六角钡铁氧体及磁性[J].应用化学,2007(10):1182-1186. |
| [11] | 李筱濛,曹全喜,王青松,王毓鹏,史学芳.M型Ba（CoTi）1.2Fe9.5Mn0.15O19的制备及吸波性能研究[J].压电与声光,2008(03):346-348,362. |
| [12] | 姚静,余利华,徐丹丹.Sm3+掺杂量对Co2Z六方铁氧体磁性能的影响[J].电子元件与材料,2009(01):44-45,52. |
| [13] | 杨永峰,黄英,郭银明,李玉青.离子掺杂钡铁氧体的研究进展[J].硅酸盐通报,2007(06):1153-1159. |
| [14] | 廖绍彬;尹光俊;刘进.多晶铁氧体微波介电损耗的研究[J].北京大学学报（自然科学版）,1979(03):52. |
| [15] | 周克省,刘利强,邓联文,黄可龙,周一平,刘宝刚.W型Ba1-xLaxCo2Fe16O27的微波吸收性能[J].中南大学学报(自然科学版),2008(06):1170-1174. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%