针对一种新型高强变形铝青铜合金,考察了淬火温度和回火温度对该合金的微观组织和力学性能的影响.研究结果表明,淬火温度越高,合金内部的β'马氏体相越多,材料的硬度越高,但淬火温度过高时,由于针片状α相的出现,使材料的强度和塑性有较大下降.试验合金适宜的淬火温度为900℃.淬火态材料经低温回火,强度可进一步提高,400℃回火时材料的强度和硬度达到峰值,此后随着回火温度的升高,材料的强度和硬度逐渐下降,延伸率逐渐提高.600℃回火态材料的抗拉强度和延伸率分别达到900 MPa和17%以上,具有优良的强韧配合.
参考文献
| [1] | 王祝堂;田荣璋.铜合金及其加工手册[M].长沙:中南大学出版社,2002:270. |
| [2] | 徐建林,王智平.铝青铜合金的研究与应用进展[J].有色金属,2004(04):51-55. |
| [3] | 宋德军,孙现龙,许磊,叶景涛,胡伟民.变形镍铝青铜合金的组织研究[J].稀有金属,2008(04):420-424. |
| [4] | Breina P .Heat treatment of complex aluminum bronzes[J].International Metals Reviews,1982,27(02):77. |
| [5] | Kaplan M;Yildiz A K .The effects of production methods on the microstruetures and mechanical properties of an aluminum bronze[J].Materials Letters,2003,57:4402. |
| [6] | 徐建林,路阳,刘明朗,李海兰,李文生,王智平,朱小武.均匀化退火对铸造高铝青铜的影响[J].航空材料学报,2006(05):26-30. |
| [7] | 何勇.QAl10-5-5铝青铜热处理工艺的研究[J].国外金属热处理,2005(02):12-15,18. |
| [8] | 刘阳,路阳,袁利华,李曙.新型高铝青铜的组织及耐磨性[J].金属热处理,2007(04):34-37. |
| [9] | 王智平,李海兰,徐建林,路阳,刘明朗.固溶时效对高铝青铜组织与性能的影响[J].铸造,2004(06):439-442. |
| [10] | Hasan F;Jahanafrooz A;Lorimer G .The morphology,crystallography,and chemistry of phases in as-cast nickel-aluminum bronze[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1982,13:1337. |
| [11] | Recarte V;Peroz-Saez R;Bocaneqra E .Influence of Al and Ni concentration on the martensitie transformation in Cu-Al-Ni shapememory alloys[J].Metathrgical and Materials Transactions A,2002,33(08):2581. |
| [12] | Kim S;Choi C H;Lee D N .Deformation and annealing textures of drawn aluminum bronze wires[J].Materials Science Forum,2002,408-412(01):913. |
| [13] | 刘淑云.铜及铜合金热处理[M].北京:机械工业出版社,1990:106. |
| [14] | Suresh N;Ramamurty U .Aging response and its effect on the functional properties of Cu-Al-Ni shape memory alloys[J].Journal of Alloys and Compounds,2008,449:113. |
| [15] | R.K. GUPTA;B.R. GHOSH;P.P. SINHA .Design of Heat Treatment Cycle for Hardness Improvement of Cu-9Al-6Ni-5Fe Alloy[J].Canadian Metallurgical Quarterly,2006(3):353-358. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%