根据涂层超导应用对Ni5W合金基带织构的要求,分析研究了轧制方式、轧制工艺润滑、轧制速度等对Ni5W合金基带轧制形变织构及再结晶立方织构的影响,研究发现,往复轧制避免了不利于形成再结晶立方织构的其他冷轧取向的产生,进而在Ni5W合金基带中获得较多的C型和S型取向,利于退火过程中获得锐利的再结晶立方织构,对比分析了非润滑轧制和润滑轧制的再结晶晶界分布情况,发现非润滑轧制较润滑轧制产生的孪晶界含量少,且晶界质量比较高,并对3种不同轧制速度的轧制结果进行了分析,得出5 m·min-1为最佳的轧制速度.提出了相应的优化轧制工艺,为轧制基带的织构控制和性能优化提供参考,最终冷轧和退火后获得了长度为20 m,厚度为～63 μm,立方织构含量达～99%(<10°),性能均匀的Ni5W合金基带,为Ni5W合金基带长带的产业化生产奠定了基础.
参考文献
| [1] | Shinichi Mukoyama;Masashi Yagi;Hironobu Hirano;Yutaka Yamada,Teruo lzumi,Yuh Shiohara .Development of HTS power cable using YBCO coated conductor[J].Physica C,2006,445-448:1050. |
| [2] | Fleshler, S;Buczek, D;Carter, B;Cedrone, P;DeMoranville, K;Gannon, J;Inch, J;Li, X;Lynch, J;Otto, A;Podtburg, E;Roy, D;Rupich, M;Sathyamurthy, S;Schreiber, J;Thieme, C;Thompson, E;Tucker, D;Nagashima, K;Ogata, M .Scale-up of 2G wire manufacturing at American Superconductor Corporation[J].Physica, C. Superconductivity and its applications,2009(15/20):1316-1321. |
| [3] | Masur LJ.;Buczek D.;Harley E.;Kodenkandath T.;Li X.;Lynch J.;Nguyen N.;Rupich M.;Schoop U.;Scudiere J.;Siegal E.;Thieme C.;Verebelyi D. Zhang W.;Kellers J. .The status of commercial and developmental HTS wires[J].Physica, C. Superconductivity and its applications,2003(Pt.2):989-997. |
| [4] | Norton DP.;Prouteau C.;Christen DK.;Chisholm MF.;Budai JD. Pennycook SJ.;Goyal A.;Sun EY.;Lee DF.;Kroeger DM.;Specht E. Paranthaman M.;Browning ND.;Park C. .Epitaxial YBa2Cu3O7 films on rolled-textured metals for high-temperature superconducting applications[J].Materials Science & Engineering, B. Solid-State Materials for Advanced Technology,1998(2/3):86-94. |
| [5] | Eickemeyer J;Selbmann D;Opitx R;Boer B De,Holzapfel B,Schultz L,Miller U .Nickel-refractory metal substrate tapes with high cube texture stability[J].Superconductor Science and Technology,2001,4:152. |
| [6] | Sarma V S;Boer B de;Reger N;Eickemeyer J Opitz R .Ni and Ni-alloy tapes with a very strong cube texture as substrates for high temperature superconducting tapes[J].Materials Science Forum,2002,408-412:1561. |
| [7] | Zhang W;Rupich MW;Schoop U;Verebelyi DT;Thieme CLH;Li X;Kodenkandath T;Huang Y;Siegal E;Buczek D .Progress in AMSC scale-up of second generation HTS wire[J].Physica, C. Superconductivity and its applications,2007(0):505-509. |
| [8] | 刘慧舟,杨坚,张华,古宏伟.移动Ni-5W基带上制备钇系涂层导体隔离层的研究[J].稀有金属,2008(05):627-630. |
| [9] | 张华,金薇,刘慧舟,冯校亮,杨坚.走带速率对Y2O3隔离层生长的影响[J].稀有金属,2009(01):35-38. |
| [10] | Doherty R D;Hughes D A;Humphreys F J;Jonas JJ,Jensen D Juul,Kassner M E,King W E,McNelley T R,McQueen H J,BollettU A D.Schmidt K .Current issues in recrysiallization:a review[J].Materials Science and Engineering A,1997,238:219. |
| [11] | Duggan B J;Lucke K;Kohlhoff G;Lee C S .On the origin of cube textuIe in copper[J].Acts Metall,1993,41:1921. |
| [12] | 毛卫民;杨平;陈冷.材料织构分析原理与检测技术[M].北京:冶金工业出版社,2008:37. |
| [13] | 陈彦博;赵红亮;翁康荣.有色金属轧制技术[M].北京:化学工业出版社,2007:210. |
| [14] | 毛卫民;杨平;陈冷.材料织构分析原理与检测技术[M].北京:冶金工业出版社,2008:12. |
| [15] | 陈彦博;赵红亮;翁康荣.有色金属轧制技术[M].北京:化学工业出版社,2007:180. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%