稀土元素及其含量对铝合金耐腐蚀性能的影响及其机制是铝合金开发利用的重要研究课题,采用高频熔炼方法制备Al1-xCex(x=0,0.2％,2.0％(原子分数))合金,通过X射线衍射、金相分析、电化学测试、扫描电镜和能谱等分别对制备的Al1-xCex合金的结构、动电位线性扫描极化曲线、浸泡与电化学腐蚀前后表面形貌的变化进行了研究；对Al1-xCex在3.5％ NaCl溶液中耐腐蚀性能与铈含量的关系进行了系统的分析.结果表明:由于Cl-离子的存在,铝在3.5％ NaCl溶液中发生点蚀破坏；稀土Ce的加入能够细化晶粒,改善合金微观结构,减弱Cl-离子对点蚀的影响；Ce元素在腐蚀表面层富集,有利于形成连续钝化膜,提高合金在NaCl溶液中的耐蚀能力；微量稀土Ce(0.2％)的加入使合金的自腐蚀电位升高,腐蚀电流密度降低,耐腐蚀性能改善明显；但随着Ce含量的增加,即含量高于铈在铝中的溶解度后,铝与铈将形成金属间化合物,基底与金属间化合物相界面的存在使合金的耐腐蚀性能有所降低,Ce含量为0.2％合金的耐腐蚀性能比Ce含量为2.0％的合金要好.所有合金腐蚀后的主要产物为Al2O3.
参考文献
| [1] | Na K H;Pyun S I .Electrochemical noise analysis of corrosion of pure aluminium in alkaline solution in the presence of SO42-ion,NO3-ion and Na2S additives[J].Electrochimica Acta,2007,52:4363. |
| [2] | Lee W J;Pyun S I .Role of prior cathodic polarization in the pitting corrosion of pure aluminium in acidic chloride solution[J].Materials Science and Engineering,2000,A279:130. |
| [3] | Moon S M;Pyun S I .The corrosion of pure aluminium during cathodic polarization in aqueous solution[J].Corrosion Science,1997,39:399. |
| [4] | Hatch J E.Aluminum:Properties and Physical Metallurgy[M].Metals Park,OH:American Society for Metals,1984 |
| [5] | Boag A P;McCulloch D G;Jamieson D N;Hearne B M Hughes A E Ryan C G Toh S K .Combined nuclear microprobe and TEM study of corrosion pit nucleation by intermetallics in aerospace aluminium alloys[J].Nuclear Instruments and Methods in Physics Research,2005,B231:457. |
| [6] | Panagopoulos C N;Georgiou E P;Gavras A G .Corrosion and wear of 6082 aluminum alloy[J].Tribology International,2009,42:886. |
| [7] | Andreatta F;Terryn H;de Wit J H W .Corrosion behavior of different tempers of AA7075 aluminium alloy[J].Electrochimica Acta,2004,49:2851. |
| [8] | Pyun S I;Lee S J .Current status and advances in corrosion researches[J].Journal of Solid State Electrochemistry,2009,13:1637. |
| [9] | Szklarska-Smialowska Z .Pitting corrosion of aluminium[J].Corrosion Science,1999,41:1743. |
| [10] | Szklarska-Smialowska Z .Insight into the pitting corrosion behavior of aluminum alloys[J].Corrosion Science,1992,33:1193. |
| [11] | Dzib-Perez L;Gonzalez-Sanchez J;Perez T;Bartolo-Perez P Juarez A .The role of solidification rate in the corrosion resistance of a directionally solidified novel aluminium-lanthanum alloy[J].Scripta Materialia,2006,55:255. |
| [12] | Banczek E P;Zarpelon L M C;Faria R N;Costa I .Corrosion resistance and microstructure characterization of rare-earth-transition metal-aluminum-magnesium alloys[J].Journal of Alloys and Compounds,2009,479:342. |
| [13] | Mishra A K;Balasubramaniam R .Conosion inhibition of aluminium by rare earth chlorides[J].Materials Chemistry and Physics,2007,103:385. |
| [14] | Arnott D R;Ryan N E;Hinton B R W;Sexton B A Hughes A E .Auger and XPS studies of cerium corrosion inhibition on 7075 aluminum alloy[J].Applied Surface Science,1985,22-23:236. |
| [15] | 张强,李聪,邱绍宇.晶粒细化对Zr-4合金均匀腐蚀性能的影响[J].稀有金属,2009(02):170-174. |
| [16] | B. Zaid;D. Saidi;A. Benzaid;S. Hadji .Effects of pH and chloride concentration on pitting corrosion of AA6061 aluminum alloy[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2008(7):1841-1847. |
| [17] | Zhou H R;Li X G;Dong C F;Xiao K .Corrosion behavior of aluminum alloys in Na2SO4 solution using the scanning electrochemical microscopy technique[J].International Journal of Minerals, Metallurgy and Materials,2009,16:84. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%