用溶胶-凝胶法合成了Ce1-xCaxO2-x(x=0~0.35)系列固体电解质,系统地研究了其晶体结构随CaO含量的变化关系.XRD测试表明,该体系于160℃即形成萤石结构纯相.高温XRD表明,从室温至800℃,Ce1-xCaxO2-x(x=0~0.35)未出现结构相变.此法合成温度远低于传统的高温固相合成法和水热合成法的温度.合成物的颗粒小,粒度均匀.在1300℃即可烧结成高致密度样品.XPS测试表明,掺杂CaO后吸附氧浓度明显增大,氧空位增多,电导率和氧离子迁移数增大,改善了CeO2基固体电解质的性能.
参考文献
[1] | Yamazoe N,Miura N. Solid State Ionics, 1996,86~88(Part Ⅱ ):987 |
[2] | Iwahara H. Solid State Ionics,1996,86~88(Part I):9 |
[3] | MIU Jian-Ying(缪建英),YANG Le-Fu(杨乐夫),CHEN Du-Hui(陈笃慧),et al. Yingyong Huax(应用化学),1998,15(4):37 |
[4] | Minh N Q. J Am Ceram Soc,1993,76(3):563 |
[5] | Meng G Y,Liu W Y,Peng D K . 97th Xiangshan Sci Conf on New SSFCs ,Beijing, 1998:1 |
[6] | Shuk P, Wiemhofer H D,Guth U, et al. Solid State Ionics, 1997,89(3~4):179 |
[7] | Inaba H,Tagawa H. Solid State Ionics,1996,83(1~2):1 |
[8] | van Herle J, Horita T, Kawada T, et al. Solid State Ionics, 1996,86~88(Part I ): 1255 |
[9] | HE Zhi-Qi(何志奇),JIANG Kai(蒋凯),MENGJian(孟健),et al. Yingyong Huaxue(应用化学),1998,15(3):22 |
[10] | Huang K,Feng M,Goodenough J B. J Am Ceram Soc, 1996,79(4):1100 |
[11] | Yahiro H, Ohuchi T, Eguchi, et al. J Mater Sci,1988,23(3): 1036 |
[12] | Huang W,Shuk P,Greenblatt M. Chem Mater,1997,9(10):2240 |
[13] | Shannon R D. Acta Cryst,1967,A32(6):751 |
[14] | Longo V,Podda L. J Am Geram Soc, 1978,61(7~8):371 |
[15] | Cook R L, Sammells A F. Solid State Ionics,1991,45(3~4):311 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%