通过改变聚酰亚胺膜中主链氟的含量,合成了几种高预倾角的聚酰亚胺膜,测定了各种膜取向前后的接触角,发现接触角随聚酰亚胺膜主链中氟含量的改变而改变. 在原子力显微镜下观察含氟聚酰亚胺及不含氟聚酰亚胺取向膜的微观结构,发现两种膜都是沿着摩擦方向有序排列,其中完全含氟聚酰亚胺取向膜较不含氟的聚酰亚胺取向膜更有规整性.
参考文献
| [1] | Fukuro H,Kobayashi S. Mol Cryst Liq Cryst,1988, 163:157 |
| [2] | Masami Y,Toshihiko K. Jpn Kokai Tokkyo Koho,TP 06 130 399 |
| [3] | Shigeki I,Misako H,Tohru M. Mol Cryst Liq Cryst,1993,225:99 |
| [4] | Castello J M. Mol Cryst Liq Cryst,1983,94:33 |
| [5] | Binnig G,Rohrer H,Gerber C, et al. Phys Rev Lett,1982,49:57 |
| [6] | Scheffer T J,Nehring J. J Appl Phys,1977,5:1 785 |
| [7] | Van Krevelen D W Auth. XU Yuan-Ze(许元泽),ZHAO De-Lu(赵得禄),WU Da-Cheng(吴大诚)Trans(译). Properties of Polymers(聚合物的性质). Beijing(北京):Science Press(科学出版社),1987:121 |
| [8] | CHENG Chuan-Xuan(程传煊)Auth(著). Surface Physical Chemistry(表面物理化学). Shanghai(上海):Science and Technology Literature Press(科学技术文献出版社),1995:110 |
| [9] | Kim Y B,Olin H,Park S Y, et al. Appl Phys Lett,1995,66:2 218 |
| [10] | Nejoh H. Surf Sci,1991,256:94 |
| [11] | Binnig G,Gerber C,Quate C F. Phys Rev Lett,1986,56:930 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%