用共沉淀法和溶胶-凝胶法制备了Fe-P-O催化剂,用DTA-TG、TEM、XRD、IR和TPR等方法对微粒组成、结构进行了表征.以分子探针IR方法考察了乙烷在Fe-P-O催化剂表面上的吸附性能.结果表明,溶胶-凝胶法制备的Fe-P-O催化剂为超细非晶态结构,粒子分布为10～20 nm,其比表面、晶格氧的活泼性均大于共沉淀法制备的晶态Fe-P-O催化剂.乙烷能以分子态吸附于催化剂表面P=O键上,随吸附温度升高,乙烷吸附强度逐渐增大;乙烷在非晶态Fe-P-O催化剂上的吸附量和吸附强度均大于晶态Fe-P-O催化剂.
参考文献
| [1] | Muneyama E, Kunishige A, Ohdan K et al. J Catal, 1996,158: 378 |
| [2] | Rouzies D,Millet J M M,Sam D S H et al. Appl Catal , 1995,124: 189 |
| [3] | Bonnet P, Millet J M M, Leclereq C et al. J Catal , 1996,158:128 |
| [4] | Wang Y,Otsuka K. J Catal,1997,171:106 |
| [5] | Millet J M. Catal Rev-Sci Eng,1998,40(1～2):1 |
| [6] | Campelo J M,Garcia A,Luna D. J Catal,1986,102:299 |
| [7] | Wang Y, Otsuka K. J Mol Catal A:Chemical,1996,111: 341 |
| [8] | Annapragada A V,Gulari E. J Catal,1990,123:130 |
| [9] | TAO Yue-Wu(陶跃武).Doctoral Dissertation ([博士学位论文]).Tianjin(天津):Tianjin University(天津大学),1999 |
| [10] | KUANG Wen-Xing(匡文兴),FAN Yi-Ning(范以宁),CHEN Kai-Dong(陈开东) et al.Wuli Huaxue Xuebao(物理化学学报),1996,12(9):861 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%