以Zn粉和FeCl3*5H2O为主要原料,采用溶剂热技术在油酸和无水乙醇的混合体系中合成了ZnFe2O4纳米微晶. 通过XRD 、TEM等测试技术对产物进行了表征,并对产物的自控合成机理进行了分析以及对产物气敏元件的气敏性进行了测试. 实验结果表明,ZnFe2O4纳米微晶的平均尺寸约为30 nm,其气敏元件在空气气氛中阻值较稳定.
参考文献
| [1] | LIU Hui(刘辉),WEI Yu(魏雨),ZHANG Yan-Feng(张艳峰), et al. J Inor Mater(无机材料学报)[J],2002,17(1):56 |
| [2] | Chu X F. Sens Actuators[J],1999,B55:19 |
| [3] | Kordas G. J Non-cryst Solids[J],1990,121:436 |
| [4] | Chen J. J Magn Magn Mater[J],1995,146:291 |
| [5] | Schiessl W. J Am Phys Soc[J],1996,53(14):9 143 |
| [6] | Anantharaman M R. J Magn Magn Mater[J],1998,189:83 |
| [7] | Gopal Reddy C V. Sens Actuators[J],1999,B55:90 |
| [8] | Sato T,Haneda K. Appl Phys A[J],1990,50:13 |
| [9] | Kumazawa H,Oki K,Cho H M, et al. Chem Eng Comm[J],1992,115:25 |
| [10] | Bhattacharya A K,Hartridga A. J Mater Sci Lett[J],1996,15(21):1 842 |
| [11] | XU Kang(徐康),LIU Jian-Jun(刘建军). J Inor Mater(无机材料学报)[J],1997,12(5):759 |
| [12] | Rozman M. J Am Ceram Soc[J],1995,78(9):2 449 |
| [13] | Moom J, et al. J Mater Res[J],1997,12(1):189 |
| [14] | Qian Y T. J Mater Res[J],1997,12(1):189 |
| [15] | LI Ya-Dong(李亚栋). Doctoral Dissertation([博士学位论文]). Hefei(合肥):University of Science ＆Technology of China(中国科学技术大学),1998 |
| [16] | JIAO Zheng(焦正),CHEN Feng(陈锋),LI Min-Qiang(李民强), et al. J Inor Mater(无机材料学报)[J],2002,17(3):316 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%