在聚四氟乙烯多孔膜模板的控制下,将0.1 mol/L的Na2S和CdCl2进行跨膜传输和分子组装,成功制得平均粒径为3.2 nm的CdS纳米粒.XRD研究表明,产物为立方闪锌矿结构;荧光光谱上在522 nm处有较强的发射光谱.经巯基乙酸修饰的CdS纳米粒在红外光谱上1 680 cm-1处具有羰基的特征峰.
参考文献
| [1] | ZHANG Li-De(张立德),MOU Ji-Mei(牟季美).Nanomaterials and Nanostructure(纳米材料和纳米结构)[M].Beijing(北京):Science Press(科学出版社),2001 |
| [2] | Tito T,Paul O,Nigel L P. Chem Mater[J] ,2001,13:3 843 |
| [3] | Wang Y,Harron N J. J Phys Chem[J] ,1991,95:525 |
| [4] | Taton T A,Mirkin C A. Science[J] ,2000,288:1 808 |
| [5] | Zancher D,Micheel C M,Alivisatos A P, et al. Nano Lett[J] ,2001,1:32 |
| [6] | Nie S,Chan W C W. Science[J] ,1998,281:2 016 |
| [7] | Bruchex M Jr,Moronne M,Gim P. Science[J] ,1998,281:2 013 |
| [8] | Li Y D,Wang Z Y,Ding Y. Inorg Chem[J] ,1999,38:4 737 |
| [9] | Gao F,Lu Q Y,Zhao D Y. Chem Phys Lett[J] ,2002,360:585 |
| [10] | Pardo-Yissar V,Katz E,Wasserman J, et al. J Am Chem Soc[J] ,2003,125(3) :622 |
| [11] | Dollefeld H,McGinley C,Almousalami S, et al. J Chem Phys[J] ,2002,117(19) :8 953 |
| [12] | WU Q S,Zheng N W,Li Y D, et al. J Membr Sci[J] ,2000,172:199 |
| [13] | Li Z,Du Y M. Mater Lett[J] ,2003,57(16/17) :2 480 |
| [14] | WU Qing-Sheng(吴庆生),ZHENG Neng-Wu(郑能武),DING Ya-Ping(丁亚平),et al.Chem J Chin Univ(高等学校化学学报)[J],2000,21(10):1 471 |
| [15] | CHEN Hong-Ming(陈红明),HUANG Xin-Fan(黄信凡),HUANG Hong-Bin(黄宏彬),et al.Chin J Nanjing Univ(南京大学学报)[J],1998,34(1):35 |
| [16] | ZHANG Yu(张宇),ZHANG Jun-Xiang(张俊祥),FU De-Gang(付德刚),et al.Chin J Inorg Chem(无机化学学报)[J],1999,15(5):595 |
| [17] | WU Qing-Sheng(吴庆生),LIU Jin-Ku(刘金库),DING Ya-Ping(丁亚平),et al.Acta Chim Sin(化学学报)[J],2003,61(11):1 824 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%