用熔融复合法制备聚丙烯/凹凸棒土纳米复合材料,用DSC法研究其非等温结晶行为,对所得的数据分别用Jeziorny法、Ozawa法和Liu法进行处理.结果表明,Jeziorny法和Liu法处理非等温结晶过程比较理想.聚丙烯及聚丙烯/凹凸棒土纳米复合材料的结晶活化能分别为194.1和162.8 kJ/mol,表明凹凸棒土的加入,降低了聚丙烯的结晶活化能,且t1/2缩短,起到了异相成核作用.
参考文献
[1] | Whiteside G M,Mathias T P,Seto C T. Science[J] ,1991,254:1 312 |
[2] | Enzel P,Bein T. J Phys Chem[J] ,1989,93:6 270 |
[3] | Kojima Y,Usuki A,Kawasumi M. J MaterRes[J] ,1993,8:1 185 |
[4] | LIU Li-Min(刘立敏),ZHU Xiao-Guang(朱晓光),QI Zong-Neng(漆宗能).Acta Polym Sin(高分子学报)[J],1999,(6) :274 |
[5] | Vaia R,Giannelis E P. Macromolecules[J] ,1997,30:8 000 |
[6] | Burnside S D,Giannelis E P. Chem Mater[J] ,1995,7:1 597 |
[7] | WANG Ping-Hua(王平华),XU Guo-Yong(徐国永).China Plast Ind(塑料工业)[J],2003,31(6):13 |
[8] | de Medeiros E S,Tocchetto R S, de Carvalho L H, et al. J Therm Anal Cal[ J ] ,2001, (66) :523 |
[9] | Ozawa T. Polymer[J] ,1971,12:150 |
[10] | Ziakicki A. Coll Polym Sci[J] ,1974,252:433 |
[11] | Mandelkern L. Crystallization of Polymers[M]. New york:Mc Graw-Hill Press,1964:254 |
[12] | Jeziorny A. Polymer[J] ,1978,19:1 142 |
[13] | Liu T X,Mo Z S,Wang S E, et al. Polym Eng Sci[ J ] ,1997 ,37 :568 |
[14] | Cebe P,Hobng S D. Polymer[J] ,1986,(27) :1 183 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%