用电化学法制备了乙醇镁配合物Mg(OEt)2-x(acac)x(acac-为乙酰丙酮基),将其乙醇溶液水解制得胶体Mg(OEt)2-x-y(OH)y(acac)x,然后在500 ℃煅烧2 h,得到纳米级MgO粉体. 通过红外光谱、热重-差热分析、X射线衍射、透射电子显微镜等测试技术对前驱体、干凝胶和纳米MgO粉体进行了表征. 结果表明,得到的前驱体、干凝胶中含有acac-基团,在470~500 ℃煅烧较为适宜;得到的纳米MgO呈单分散结构,粒径为15~20 nm.
参考文献
[1] | WU Guang-Ming(武光明),FU Xiao-Rong(符晓荣),LIN Cheng-Lu(林成鲁). Funct Mater(功能材料)[J],1999,30(6):631 |
[2] | ZHU Ya-Xian(朱亚先),ZENG Ren-Jie(曾人杰),LIU Xin-Jin(刘新锦). J Xiamen Univ(厦门大学学报)[J],2001,40(6):1 256 |
[3] | JIU Jin-Ting(酒金婷),LI Li-Ping(李立平),GE Yue(葛钥), et al. Chin J Inorg Chem(无机化学学报)[J],2001,17(3):361 |
[4] | Stengl V,Bakardjieva S,Marikova M, et al. Mater Lett[J],2003,57:3 998 |
[5] | Wanga J A,Novaro O,Bokhimi X, et al. Mater Lett[J],1998,35:317 |
[6] | XU Bing-She(许并社). General Material Science(材料科学概论)[M]. Beijing(北京):Beijing Industry University Press(北京工业大学出版社),2002:164 |
[7] | Livage J,Sanchez C. J Non-Cryst Solids[J],1992,145:11 |
[8] | Mehrotra R C. J Non-Cryst Solids[J],1992,145:1 |
[9] | CHU Dao-Bao(褚道葆),ZHOU Xing-Fu(周幸福),LIN Chang-Jian(林昌健). Chem J Chin Univ(高等学校化学学报)[J],2000,1:133 |
[10] | LI Di(李荻). Electrochem Principle(电化学原理)[M]. Beijing(北京):Beijing Aerospace University Press(北京航空航天大学出版社),1998:416 |
[11] | John Errington R,Ridland J,Clegg W. Polyhedron[J],1998,5~6:659 |
[12] | YANG Yong-Lai(杨咏来),NING Gui-Ling(宁桂玲),L Jian-Ling(吕兼玲). J Mater Guide(材料导报)[J],1998,12(2):11 |
[13] | Ulrich D R. J Non-Crystalline Solids[J],1988,100:174 |
[14] | SONG Xiu-Qin(宋秀芹),CHEN Ru-Fen(陈汝芬),JIA Mi-Ying(贾密英). Chin J Appl Chem(应用化学)[J],2000,17(3):304 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%