采用溶胶-凝胶法合成锂离子电池正极材料LiNi0.45Co0.1Mn0.45O2,研究了制备条件对其物理和电化学性能的影响. 利用XRD对其进行了结构特征的表征,并且采用DSC、恒流充放电、循环伏安等多种分析手段对合成的LiNi0.45Co0.1Mn0.45O2进行了测量. 结果表明,在700 ℃煅烧7 h合成出的正极材料LiNi0.45Co0.1-Mn0.45O2,在3.0~4.3 V循环30次后放电容量仍保持145 mA*h/g.
参考文献
[1] | LIU Pei-Song(刘培松),LIU Xing-Quan(刘兴泉),CHEN Zhao-Yong(陈召勇), et al. Chin J Appl Chem(应用化学)[J],2003,20(12):1 171 |
[2] | XIA Xiao-Yong(夏小勇),WEI Jin-Ping(魏进平),YE Mao(叶茂), et al. Chin J Appl Chem(应用化学)[J],2003,20(10):928 |
[3] | Jing Z,Abraham K M. J Electrochem Soc[J],1996,143(5):1 591 |
[4] | Macneil D D,Lu Z,Dahn J R. J Electrochem Soc[J],2002,149:A1 332 |
[5] | Shaju K M,Subba rao G V,Chowdari B V R. Electrochim Acta[J],2003,48:1 505 |
[6] | Sang H P,Sun Y-K. J Power Sources[J],2003,119~121:161 |
[7] | Chen Y,Wang G X,Konstantinov K, et al. J Power Sources[J],2003,119~121:184 |
[8] | Lu Z H,Donaberger R A,Thomas C T, et al. J Electrochem Soc[J],2003,149:A1 082 |
[9] | Paulsen M,Thomas C L,Dahn J R. J Electrochem Soc[J],2000,147:861 |
[10] | Kim J-H,Park C W,Sun Y-K. Solid State Ionics[J],2003,164:43 |
[11] | Kim J-S,Johnson C S,Thackeray M M. Electrochem Commun[J],2002,4:205 |
[12] | Lu Z H,Macneil D D,Dahn J R. J Electrochem Solid-state Lett[J],2001,4:A200 |
[13] | Kang S-H,Kim J,Stoll M E, et al. J Power Sources[J],2002,112:41 |
[14] | Kang S-H,Amine K. J Power Sources[J],2003,119~121:150 |
[15] | Naokaki Y,Tsutomu O. J Power Sources[J],2003,119~121:171 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%