用过二硫酸铵((NH4)2S2O8)氧化Mn(Ⅱ)盐制备δ-MnO2. 比较了反应过程中Mn2+与OH-的摩尔比、反应温度、(NH4)2S2O8用量等因素对MnO2晶型的影响. 用X射线衍射(XRD)、红外光谱(IR)分析了制得的δ-MnO2的结构. 测试了样品的热性能和循环伏安、恒电流充放电性能. 结果表明所制备的δ-MnO2具有良好的层状结构,热稳定性能较好,放电容量较高(约160 mA·h/g,2.0～4.5 V).
参考文献
| [1] | Nazar L F,Wu H,Power W P. Mater Chem[J],1995,5(11):1 985 |
| [2] | Kerr T A,Wu H,Nazar L F. Chem Mater[J],1996,8:2 005 |
| [3] | Bach S,Peraira-Ramos T P,Baffier N. J Electrochem Soc[J],1996,143(11):3 429 |
| [4] | Ching S,Landrigan J A,Jorgeuse M L. Chem Mater[J],1995,7:1 604 |
| [5] | Gaff P L,Baffier N,Bach S, et al. J Mater Chem[J],1994,4(6):875 |
| [6] | LI Qing-Wen(李清文),ZHANG Bo(张波),SHU Dong(舒东). Chin J Battery(电池)[J],1993,123:203 |
| [7] | Shen Y F,Zerger R P,DeCuzman R, et al. Science[J],1993,260:511 |
| [8] | YANG Yong(杨勇),SHU Dong(舒东),YU Hai(余海), et al. Chin J Power Sources(电源技术)[J],1997,21:190 |
| [9] | LIU Bin(刘斌),XIA Xi(夏熙). Chin J Battery Ind(电池工业)[J],2000,5(4):152 |
| [10] | Rongji C,Chirayil T,Zavalij P, et al. Solid State Ionics[J],1996,140(7):86 |
| [11] | Vitins G,West K. J Electrochem Soc[J],1997,144:2 587 |
| [12] | Renuka R,Ramamurthy S. J Power Sources[J],2000,91(87):144 |
| [13] | Komaba S,Kumagai N,Chiba S. Electrochim Acta[J],2000,46:31 |
| [14] | ZHANG Qi-Wei(张启卫),ZHANG Yong-Hua(章永化),CHEN Shou-Ming(陈守明). Chin J Inorg Salt Ind(无机盐工业),2003,35(1):25 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%