合成了一种新型的聚醚酰亚胺(PEI-A),使之以10%～50%的质量分数与双马来酰亚胺(BMI)单体+烯丙基双酚A(DBA)体系共混,经由反应诱导相分离(160 ℃、8 h,185 ℃、2 h,200 ℃、10 h),制得粒径为3～5 μm 无孔BMI树脂微球. 用SEM观察了共混物的相结构和BMI树脂微球的形态,用激光粒度仪测定了BMI树脂微球的粒度及其分布. 结果表明,随着PEI-A用量的增加,BMI树脂微球粒径减小,且粒度分布呈由不均匀到均匀再到不均匀的变化.
参考文献
| [1] | Gong B,Wang L,Wang C,et al. J Chromatogr A[J],2004,1 022:33 |
| [2] | Nesterenko P N,Kebets P A,Sochilinea K O.Zhurnal Analiticheskoj Khimii[J],2003,58:523 |
| [3] | Zhang S,Huang X,Yao N,et al. J Chromatogr A[J],2002,948:193 |
| [4] | SUI Xi-Hua(隋希华),HUANG Tian-Bao(黄天宝).Chin J Synth Chem(合成化学)[J],1998,3:302 |
| [5] | GUO Yu-Han(郭予含),YANG Yan-Guo(杨彦果),SU Tian-Sheng(苏天升).Acta Polym Sin(高分子学报)[J],2000,5:641 |
| [6] | YANG Zhen-Zhong(杨振忠),XU Yuan-Ze(许元泽),YU Hao(俞浩),et al. Acta Polym Sin(高分子学报)[J],1997,1:199 |
| [7] | QIU Dong(邱东),LI Jun(李君),YANG Zhen-Zhong(杨振忠).Acta Polym Sin(高分子学报)[J],2002,5:699 |
| [8] | Xu J,Wu H,Mills O P,et al. J Appl Polym Sci[J],1999,72(8):1 065 |
| [9] | Jin J,Cui J,Tang X,et al. J Appl Polym Sci[J],2001,81(2):350 |
| [10] | Luo Y,Li S.J Macromol Sci Pure and Appl Chem[J],2002,39:825 |
| [11] | HU Jie(胡杰),LIU Bai-Ling(刘百玲),WANG Di-Qiang(汪地强).Acta Polym Sin(高分子学报)[J],2003,4:540 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%