以丙烯酸酯类单体及γ-甲基丙烯酰氧基丙基三甲氧基硅烷(A-174)等为原料,乳液聚合制备了有机硅改性的核-壳型聚丙烯酸酯乳液(简称ACR乳液),考察了ACR乳液质量分数、交联剂质量分数、固化温度及固化时间等因素对其固砂效果的影响. 结果表明,当ACR乳液质量分数为1.2%,交联剂质量分数为3%,固化温度为65 ℃,固化时间为6 h时,固结砂柱渗透率损失最小. 在50 mL/min流量下的冲砂实验中不出砂,呈现出良好的固砂性能.
参考文献
| [1] | HU Yu-Guo(胡玉国),DENG Da-Zhi(邓大志),SU Hui(宿辉),et al.Fine Specialty Chem(精细与专用化学品)[J],2002,(23):14 |
| [2] | Osman E A,et al Auths(著).GONG Rong-Hui(龚荣辉),WANG Min(王敏),et al Trans(译).Special Oil Gas Reservoirs(特种油气藏)[J],2001,8(3):1 014 |
| [3] | LI Le-Mei(李乐梅),LI Jian-Kang(李建康),L(U) Jian-Hai(吕健海),et al.Oilfield Chem(油田化学)[J],2004,21(2):103 |
| [4] | ZHOU Ai-Lian(周爱莲),ZHAO Xiu-Tai(赵修太),LI Ke-Hua(李克华).Drilling Production Tech(铝采工艺)[J],2000,23(6):60 |
| [5] | Joseph A A,John P C,Paul W W.US 6 632 778[P],2003 |
| [6] | Paul S.US 5 522 460[P],1996 |
| [7] | Alfred R J,Eve S S,Robert S T.US 5 363 917[P],1994 |
| [8] | John M D.US 5 178 218[P],1993 |
| [9] | Robin W H,Durai N R.US 5 048 608[P],1991 |
| [10] | Jimmie D W,Joseph R M.US 4 936 385[P],1991 |
| [11] | CAO Tong-Yu(曹同玉),LIU Qing-Pu(刘庆普),HU Jin-Sheng(胡金生)Edrs(编).Synthesis Principle of Polymer Latex and It′s Property and Application(聚合物乳液合成原理、性能及应用)[M],Chapt.12(第12章).Beijing(北京):Chemical Industry Press(化学工业出版社),1997 |
| [12] | MA Kang-Ming(马康铭),LI Ying(李英).Fine Chem(精细化工)[J],1991,8(6):12 |
| [13] | DAI Cai-Li(戴彩丽),ZHANG Gui-Cai(张贵才),ZHZO Fu-Lin(赵福麟).Oilfield Chem(油田化学)[J],2000,17(4):292 |
| [14] | GONG Xing-Yu(龚兴宇),FAN Xiao-Dong(范晓东).Polym Mater Sci Eng(高分子材料科学与工程)[J],2003,19(1):61 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%