通过热引发甲基丙烯酸环戊基-立方低聚倍半硅氧烷(R7R′Si8O12或POSS)(MA-POSS)与臭氧预处理的含氟聚酰亚胺(6F-Durene)自由基接枝共聚制得6F-Durene共价接枝包含立方低聚倍半硅氧烷(POSS)的聚甲基丙烯酸酯(PMA)支链的纳米复合物. 用核磁共振(NMR)、X射线衍射(XRD)和场发射扫描电子显微镜(FESEM)等测试技术分别对POSS/6F-Durene纳米复合物进行了结构表征及形貌观察. POSS/6F-Durene纳米复合物薄膜与未接枝的6F-Durene薄膜相比具有更低的介电常数ε(在2.5～2.0范围内).
参考文献
| [1] | Wang Z,Mitra A,Wang H,et al.Adv Mater[J],2001,13:1 463 |
| [2] | Loo L S,Gleason K K.Electrochem Solid-State Lett[J],2001,4:G81 |
| [3] | Connor E F,Sundberg L K,Kim H-C,et al.Angew Chem Int Ed[J],2003,42:3 785 |
| [4] | Gagliani J,Supkis D E.Adv Astronaut Sci[J],1979,38:193 |
| [5] | Krutchen C M,Wu P.US 4 535 100[P],1985 |
| [6] | Narkis M,Paterman M,Boneh H,et al.Polym Eng Sci[J],1982,22:417 |
| [7] | Hedrick J L,Carter K R,Richter R,et al.Chem Mater[J],1998,10:39 |
| [8] | Chen Y W,Wang W C,Yu W H,et al.Adv Funct Mater[J],2004,14:471 |
| [9] | Chen Y W,Wang W C,Yu W H,et al.J Mater Chem[J],2004,14:1 406 |
| [10] | Zhang C,Babonneau F,Bonhomme C,et al.J Am Chem Soc[J],1998,120:8 380 |
| [11] | Leu C M,Reddy G M,Wei K H,et al.Chem Mater[J],2003,15:2 261 |
| [12] | Uyama Y,Kato K,Ikada Y.Adv Polym Sci[J],1998,137:1 |
| [13] | Boutevin B,Robin J J,Torres N,et al.Polym Eng Sci[J],2002,42:78 |
| [14] | Vora R H,Krishnan P S G,Goh S H,et al.Adv Funct Mater[J],2001,11:361 |
| [15] | Wang W C,Vora R H,Kang E T,et al.Ind Eng Chem Res[J],2003,42:784 |
| [16] | Zheng L,Waddon A J,Farris R J,et al.Macromolecules[J],2002,35:2 375 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%