用三甲基氯硅烷,二甲基二氯硅烷对全硅介孔分子筛KIT-1进行了有机硅烷化,制备出疏水性介孔分子筛KIT-1. FT-IR图谱显示,硅烷基已接枝到了分子筛孔道表面,XRD和低温N2吸附-脱附表明硅烷化样品仍保持了基体KIT-1完整的介孔孔道结构,但BET比表面积和BJH孔容、孔径均有所下降. 硅烷化介孔分子筛表现出较高的抗水解能力(沸水中处理48 h以上仍保持完整的介孔结构). 用三甲基氯硅烷改性的分子筛其疏水性比用二甲基二氯硅烷改性的好,对水溶液中三混甲酚的饱和吸附量为0.512 mmol/g.
参考文献
| [1] | Liu Y,Zhang W Z,Thomas J Pinnavaia.J Am Chem Soc[J],2000,122:8 791 |
| [2] | Zhang Z T,Han Y,Zhu L,et al.Angew Chem Int Ed[J],2001,40(7):1 258 |
| [3] | Li D F,Han Y,Song J W,et al.Chem Eur J[J],2004,10:5 911 |
| [4] | Han Y,Wu S,Sun Y Y,et al.Chem Mater[J],2002,14:1 144 |
| [5] | SONG Wei-Ming(宋伟明),DENG Qi-Gang(邓启刚),ZHAO De-Feng(赵德丰).Chinese J Appl Chem(应用化学)[J],2005,22(4):407 |
| [6] | Toyoshi Shimada,Kazuko Aoki,Yo Shinoda,et al.J Am Chem Soc[J],2003,125:4 688 |
| [7] | Wight A P,Davis M E.Chem Rev[J],2002,102:3 589 |
| [8] | Zhao X S,Lu G Q.J Phys Chem B[J],1998,102:1 556 |
| [9] | Yang H Q,Zhang G Y,Hong X L,et al.Microporous Mesoporous Mater[J],2004,68:119 |
| [10] | Bart H Wouters,Tiehong Chen,Muriel Dewilde,et al.Microporous Mesoporous Mater[J],2001,44～45:453 |
| [11] | Zhao X S,Lu G Q,Hu X.Microporous Mesoporous Mater[J],2000,41:37 |
| [12] | Hiromi Yamashita,Kazuhiro Maekawa,Hidetoshi Nakao,et al.Appl Surface Sci[J],2004,237:393 |
| [13] | Ryoo R,Kim J M,Shin C H,et al.Stud Surf Sci Catal[J],1997,105:45 |
| [14] | Chen J,Li Q,Xu R,et al.Angew Chem Int Ed Engl[J],1995,34:2 694 |
| [15] | LI Hui-Yun(李惠云),SUN Yu(孙渝),YUE Ying-Hong(乐英红),et al.Chem J Chinese Univ(高等学校化学学报)[J],1999,20:272 |
| [16] | FENG Hai-Feng(冯海峰),JIANG Zhong-Yi(姜忠义),LI Duo(李多),et al.Chinese J Appl Chem(应用化学)[J],2003,20(10):932 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%